Cuo/Sn0.8ti0.2o2 Catalyst: Characterization And Catalytic Performance In No Plus Co Reaction
YanRong Jia,XiaoYuan Jiang,Xiaoming Zheng
2006-01-01
Chinese journal of inorganic chemistry
Abstract:Reducibility and characteristics of CuO/Sn0.8Ti0.2O2 catalysts were examined by using a microreactor-GC NO+CO reaction system, BET, TG-DTA, FTIR, XRD and H-2-TPR techniques. CuO/Sn0.8Ti0.2O2 had high activity in NO+CO reaction, showing 93% NO conversion at 300 degrees C in air, and 100% NO conversion at 225 degrees C after H-2 pretreatment. The pore size distribution of Sn0.8Ti0.2O2 was mainly as micro-pores and ineso-pores (1 similar to 5 nm), and the specific surface area and total pore volume of Sn0.8Ti0.2O2 were 69 m(2)center dot g(-1) and 0.15 em(3) center dot g(-1), respectively. As shown by XRD analysis, there was no CuO crystal diffraction peak at 9%CuO loading, but two CuO crystal diffraction peaks at 2 theta 35.5 degrees and 38.7 degrees were present at 12% CuO loading. FTIR detected the adsorption of NO and CO on the surface of reduced 12%CuO/Sn0.8Ti0.2O2. The CU2+ sites and support surface adsorbed NO, and the process of NO adsorption led to the formation of N2O and NO3-. In contrast, the Cu+,Cu-0 sites and support surface adsorbed CO, and when the mixed gases of NO and CO were adsorbed by support surface, no NO3- was formed. H-2-TPR showed four reduction peaks (alpha, beta, gamma and delta). The alpha, beta and gamma peaks were the reductions of CuO species, and the delta peak was the reduction of Sn0.8Ti0.2O2.