Studies of the activities of CuO/Ti0.5Zr0.50 2 catalysts for NO + CO reaction

GuangHui Ding,XiaoYuan Jiang,Nianda Lin,Ben Wu,Xiaoming Zheng

2003-01-01

Abstract:In this paper, the CuO/Ti0.5 Zr0.502 catalysts were prepared for the catalytic reduction of NO by CO. Its reducibility and thermal stabilities were examined by using a microreactor-Gc NO + CO reaction system, TPR, TG-DTA and NO-TPD methods.The results show that the Cu loading and calcination temperature have the effects on the catalytic activity. The NO conversion reaches 100% when the reaction temperature of 30% CuO/Ti0.5 Zr0.5O2 (500°C 2h) is 400°C . TPR profiles indicate that there are two peaks (α β) when the Cu loading less than or equal to 12% ; whereas the catalyst with higher Cu loading display have another peak (γ) at about 300°C . The a peak is attributed to the reduction of high dispersed CuO species, the β peak is the reduction of isolated CuO species, the γ peak is the reduction of crystal CuO. TG-DTA curve shows that the exothermic peak appeared at about 725° is the completeness of crystalline ZrTiO3. The results of NO-TPD spectra indicate that NO on TZ appears two desorption peaks, while NO on 12% CuO/TZ catalysts calcined at 500 ° C and 750 ° C respectively appears three desorption peaks, it only appears two desorption peaks on catalysts calcined at 850 ° C and 950° C . And the desorption peaks temperature of NO on the above catalysts at different calcination temperature is lower than that of carrier,which indicate that the decomposition activity of NO on the CuO/TZ catalyst is higher than that of on the Ti0.5Zr 0.502 .