Effect of Pretreatment Atmosphere on CuO/TiO 2 Activities in NO + CO Reaction

Jiang Xiaoyuan,Jia Yanrong,Huang Pei Hua,Zheng Xiaoming

DOI: https://doi.org/10.1007/s10562-005-7947-7

IF: 2.936

2005-01-01

Catalysis Letters

Abstract:Using TiO 2 as carrier, CuO/TiO 2 catalysts with different CuO loading were prepared by the impregnation method. The catalytic activities in NO+CO reaction were examined with a micro-reactor gas chromatography reaction system and the methods of TPR, XPS and NO-TPD. It was found that the catalytic activities were affected by pretreatment atmosphere, i.e. H 2 atmosphere > reduction–reoxidation > 10%CO/He > reaction gas (fresh sample). NO decomposition was better by low-valence Cu species than by high-valence Cu species, i.e. Cu 0 >Cu + >Cu 2+ . The XPS results indicated that Cu species on CuO/TiO 2 were Cu 0 , Cu + , normal Cu 2+ (Cu 2+ (I)) and chain-structured Cu 2+ (Cu 2+ (II)) as –Cu–O–Ti–O–. The activities of Cu 2+ (II) were much higher than that of Cu 2+ (I), but both species were very unstable in the reaction atmosphere and easily reduced by CO, which accounted for the variable activities of fresh catalysts with increasing reaction temperature. In NO+CO reaction, the redox process was a cycle of Cu + –Cu 2+ (I) at low reaction temperature but was a cycle of Cu 0 –Cu + at high reaction temperature. As shown by NO-TPD, high catalytic activities could be attributed to the following factors, e.g. oxygen caves on the catalyst’s surface after pretreatment with H 2 and reduction–reoxidation, formation of Cu 0 after pretreatment with H 2 , and increment of Cu species dispersion and formation of Cu 2+ (II) after pretreatment with reduction–reoxidation.