Preparation and Characterization of Ce_0.3Ti_0.7O₂ and Supported CuO Catalysts for NO+CO Reaction

Xiaoyuan Jiang,Liping Lou,Yingxu Chen,Xiaoming Zheng

DOI: https://doi.org/10.1023/B:CATL.0000019330.20466.87

IF: 2.936

2004-01-01

Catalysis Letters

Abstract:The Ce x Ti1−xO2 mixed oxides at different mole ratios (x=0.1–1.0) were prepared by co-precipitation of TiCl4 and Ce(NO3)3. The structural and reductive properties of the Ce x Ti1− x O2 were affected by calcination temperature. At x=0.1–0.3, CeTi2O6 phase was formed and mainly as amorphous after calcination at 650°C. At x=0.3, only CeTi2O6 was formed after calcination at 750°C and CeTi2O6 crystallized completely after calcination at 800°C. TPR analyses showed that the amount of H2 consumption by Ce x Ti1−xO2 (650°C) (except x=0.1) was greater than that by single CeO2, and the valence of CeO2was the lowest (+3.18) at x=0.3. CuO/Ce0.3Ti0.7O2 was prepared by the impregnation method and catalytic properties were examined by means of a GC micro-reactor NO+CO reaction system, BET, TPR, XRD, XPS and NO-TPD. It was found that CuO/Ce0.3Ti0.7O2 calcined at 650°C had the highest activity in NO+CO reaction with 100% NO conversion at reaction temperature of 300°C, and at 650°C Ce0.3Ti0.7O2just began to crystallize. The catalytic activities were largely affected by the pre-treatment conditions. At low reduction temperature (100°C), CuO species was difficult to reduce. When high degree of reductions took place, both CuO species and Ce0.3Ti0.7O2 reduced and thus a part of CuO species on the support surface would be covered. The XPS and NO-TPD analyses showed that CuO/Ce0.3Ti0.7O2 had four NO absorption centers (Cu+, Cu2+(I), Cu2+(II) and Ce3+). The CuO species involving in NO+CO reaction included Cu2+(I) and Cu+, and CeO2 species (Ce3+ and Ce4+).