Preparation and property of nano-sicp / a 356 composites synthesized with a new process

Du Yuan,Kun Hu,Shulin Lv,Qi Gao,Shusen Wu

2017-01-01

Abstract:Nano-SiC particles reinforced A356 aluminum alloy composites were prepared by molten-metal process, combined with high energy ball milling and ultrasonic vibration methods. The nano particles were β-SiCp with an average diameter of 40nm, and pre-oxidized at about 850°C to form an oxide layer with thickness of approximately 4nm. The millimeter sized composite granules containing nano-SiCp were firstly produced by milling the mixture of oxidized nano-SiCp and pure Al powders, and then were remelted in the matrix-metal melt with mechanical stirring and treated by ultrasonic vibration to prepare the composite. The SEM analysis results show that SiC nanoparticles are dispersed well in the matrix and no serious agglomeration is observed. The tensile strength and elongation of the composites are increased with the increase of reinforcement fraction of SiCp ,and 2wt.% nano-SiCp are improved by 19.5% and 43.5% respectively compared with the A356 alloy