Effects of SiC Nanoparticle Content on the Microstructure and Tensile Mechanical Properties of Ultrafine Grained AA6063-SiCnp Nanocomposites Fabricated by Powder Metallurgy

X. Yao,Z. Zhang,Y. F. Zheng,C. Kong,M. Z. Quadir,J. M. Liang,Y. H. Chen,P. Munroe,D. L. Zhang

DOI: https://doi.org/10.1016/j.jmst.2016.09.022

2016-01-01

Journal of Material Science and Technology

Abstract:Ultrafine grained AA6063-SiC np nanocomposites with 1, 5 and 10 vol.% SiC np have been fabricated by a novel powder metallurgy process. This process combines high energy ball milling of a mixture of 6063 alloy granules made from machining chips and Si C nanoparticles and thermomechanical powder consolidation by spark plasma sintering and hot extrusion. The microstructure and tensile mechanical properties of the samples were investigated in detail. Increasing the Si C nanoparticle content from 1 to 10 vol.%,the yield strength and ultimate tensile strength increased from 296 and 343 MPa to 545 and 603 MPa respectively, and the elongation to fracture decreased from 10.0%, to 2.3%. As expected, a higher Si C nanoparticle content generates a stronger inhibiting effect to grain growth during the thermomechanical powder consolidation process. Analysis of the contributions of various strengthening mechanisms shows that a higher Si C nanoparticle content leads to a higher contribution from nanoparticle strengthening, but grain boundary strengthening still makes the largest contribution to the strength of the nanocomposite.When the Si C nanoparticle content increased to 10 vol.%, the failure of the nanocomposite was initiated at weakly-bonded interparticle boundaries（IPBs）, indicating that with a high flow stress during tensile deformation, the failure of the material is more sensitive to the presence of weakly-bonded IPBs.