Abstract:Materials with high specific strength and toughness are urgently needed in the fields of electronic packaging, armor, and aerospace. SiC/Al composites show good potential for these applications but the problem of mutual exclusion of strength and toughness still needs to be solved. Herein, we propose a new strategy to simultaneously enhance its strength and toughness from the perspective of structural optimization and interface enhancement. Inspired by the nacre structure, a 3D-(SiC-Si3N4)/Al co-continuous composite was prepared by freeze-casting combined with the pressure infiltration method. During the process, elongated Si3N4 grains were introduced into the ceramic framework to design the internal lamella wall structure and increase the contact area with the aluminum substrate. Moreover, a favorable interfacial bonding was designed between Si3N4 and Al to improve interface wettability. The reliable microstructure of porous 3D-(SiC-Si3N4) preform was tailored through the adjustment of initial solid loading and the alpha-Si3N4 component. The effects of initial solid loading and the alpha-Si3N4 component on the microstructure, interfacial wettability, and mechanical properties of the final composites were investigated. The results showed that the SiC-Si3N4/Al composites possess high flexural strength (769 MPa) and fracture toughness (15.1 MPa m1/2), which is superior to data reported in general literature. Numerous elongated beta-Si3N4 grains are produced on the ceramic skeleton, forming an interlocking structure with the aluminum matrix, which increases the contact area with the aluminum substrate. A chemical reaction layer was formed at the interface of the composite, greatly improving the interfacial bonding strength. This work provides a promising design guideline for developing and optimizing high-strength and tough composite.

Synthesis of Self-Toughness Porous Si3N4 Ceramics with Three-Dimensional Cage Structures

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Design and fabrication of porous Si3N4-Si2N2O in situ composite ceramics with improved toughness

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Microstructure and Mechanical Properties of Three Porous Si3n4 Ceramics Fabricated by Different Techniques

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

High-strength Porous Si 3 N 4 Ceramics Prepared by Freeze Casting and Silicon Powder Nitridation Process

Design of crack deflection induced high toughness laminated Si3N4 ceramics based on hollow oriented one-dimensional microstructure

A new approach for the net-shape fabrication of porous Si3N4 bonded SiC ceramics with high strength

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

SiC Ceramics Strengthened and Toughened with a Crystallized Intergranular Phase Network Structure

A Novel Method of Strong and Tough Si3N4 Ceramic from the Particle‐stabilized Foam

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Strong and Tough 3D-(Sic-si3n4)/al Co-Continuous Composite with Enhanced Interfaces

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Fabrication and Mechanical Properties of SiC Reinforced Reaction-Bonded Silicon Nitride Based Ceramics

POROUS Si3N4-SiO2 COMPOSITE CERAMIC AND ITS PROPERTIES

Fracture Behavior of Porous Si3n4 Ceramics with Random and Aligned Microstructure

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

Mechanical Properties and Toughening Mechanisms of Si 3 N 4 Matrix Laminated Ceramic Composite