Abstract:Porous Si3N4 ceramics are widely applied in many fields owing to their excellent properties such as high electromagnetic wave permeability, oxidation resistance, and wear resistance. Besides, the vat photopolymerization (VPP) technique can fabricate porous Si3N4-based ceramics with complex shapes and high precision. Nevertheless, The high absorptivity and refractive index of Si3N4 to ultraviolet light make it difficult to form porous Si3N4-based ceramics with the VPP technique. In this work, the addition of ZrO2 simultaneously improved the printability of Si3N4 slurries and the performance of Si3N4 ceramics via VPP technology. Rheological behavior and curing properties of the slurries were investigated, and the influence of ZrO2 content on the mechanical properties of printed Si3N4-based ceramics was investigated systematically. The addition of ZrO2 decreased the UV absorptivity of composite powder, thus improving the curing depth from 25.2 +/- 2.6 mu m to 64.8 +/- 3.7 mu m. XRD analysis revealed that ZrO2 in the composite ceramics mainly exists as the phase of yttria-stabilized tetragonal zirconia (Zr0.92Y0.08O1.96), which could ensure the effect of phase transformation toughening. With the increase of ZrO2 content, flexural strength and fracture toughness of porous Si3N4-based ceramics exhibited a trend of increase first and then decrease. As ZrO2 content increased to 10 wt%, the flexural strength and fracture toughness of porous Si3N4-based ceramics were improved from 214.7 MPa and 4.23 MPa center dot m1/2 to 345.0 MPa and 5.69 MPa center dot m1/2, respectively. Therefore, this work provided an important reference for the fabrication of highperformance porous Si3N4-based ceramic components with complex structures.

Design and fabrication of porous Si3N4-Si2N2O in situ composite ceramics with improved toughness

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Improved Properties and Microstructure of Porous Silicon Nitride/silicon Oxide Composites Prepared by Sol–gel Route

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

ZrO2 Reinforced Porous Si3N4-based Ceramics with Improved Mechanical Properties Fabricated Via Vat Photopolymerization (VPP)

Fabrication of Porous Silicon Nitride Ceramics with Gradient Microstructure

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Synthesis of Self-Toughness Porous Si3N4 Ceramics with Three-Dimensional Cage Structures

POROUS Si3N4-SiO2 COMPOSITE CERAMIC AND ITS PROPERTIES

Preparation and mechanical behavior of Si 3 N 4 composite ceramics with brick‐and‐mortar structure

Fabrication and properties of Si3N4f/RBSN porous ceramic composite

Microstructure and mechanical properties of /-Si<sub>3</sub>N<sub>4</sub> composite ceramics with novel ternary additives prepared via spark plasma sintering

Enhancing fracture toughness of silicon nitride ceramics by addition of β-Si3N4 whisker and MXene

Preparation and Mechanical Behavior of Si3N4 Composite Ceramics with Brick‐and‐mortar Structure

Microstructure and Mechanical Properties of Three Porous Si3n4 Ceramics Fabricated by Different Techniques

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)