Abstract:This work describes a viable hydrogen-induced sensitisation process toward stress corrosion cracking in chromia-forming nickel base alloys owing to oxidation by water. A mechanistic chemical understanding of the stress corrosion based on repeated cracking and re-healing of the oxide scale emerges from experiment-guided first-principles calculations. Piggybacking processes during repeated oxide scale cracking-healing cycles are understood to cause sensitisation towards the formation and growth of macroscopic cracks. Under light-water reactor conditions, the healed oxide scale comprises an outer region composed of chromium depleted nickel ferrite, and non-protective chromia, nickel oxide, nickel hydroxide. An inner nickel iron chromite layer provides the passivating barrier that controls the oxidation rate at a steady state. Early during the re-healing of a crack in the oxide scale, water is conveyed to the alloy/scale interface by hydration/dehydration of composite nickel oxy-hydroxide Ni(OH) 2 ∙NiO inclusions in the scale. At later stages, Ni(OH) 2 ∙NiO serves as oxidant of preferentially chromium, while hydrogen is released as H 2 (g) into the primary water or becomes picked up by the alloy, possibly while assisting in the reduction of NiO to form nickel metal particles. Oxidation by water equivalents at the confining alloy/scale interface favours hydrogen pick-up in the alloy that becomes increasingly detrimental owing to enrichment and inward diffusion of hydrogen along alloy grain boundaries where pinning of alloy vacancies causes mitigation of outward diffusion of chromium, which in turn hampers crack re-healing while promoting alloy embrittlement.

Stress Corrosion Cracking of High-Strength Ni-Base Alloys in PWR Primary Water Containing KOH vs. LiOH

The effect of potassium hydroxide primary water chemistry on the IASCC behavior of 304 stainless steel

Irradiation Assisted Stress Corrosion Cracking of 347 Stainless Steel in Simulated PWR Primary Water containing Lithium Hydroxide or Potassium Hydroxide

Quantification of SCC mechanisms in austenitic alloys under PWR primary water conditions

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Stress corrosion crack initiation in Alloy 690 in high temperature water

Effects of composition and microstructure on oxidation and stress corrosion cracking susceptibility of stainless steel claddings in hydrogenated PWR primary water

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690

Corrosion Mechanism and Electrochemical Reactions on Alloy 690 in Simulated Primary Coolant of Water–Water Energy Reactors

Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment

Stress Corrosion Cracking Behavior of TP 439 and 690 TT under Film-Forming Amine Environment

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads

Effect of zinc injection on mitigating stress corrosion cracking initiation of structural materials in light water reactor primary water

Effect of material chemical composition on oxidation and stress corrosion cracking of the submerged arc welding Alloy 52M overlay in a simulated PWR primary water

Effect of dissolved oxygen and hydrogen on the stress corrosion cracking behavior of alloy 600 in high temperature water

Influence of AC/DC on stress corrosion cracking of Ti-6Al-3Nb-2Zr-1Mo alloy in simulated marine solution

Corrosion behavior of nickel base alloys, stainless steel and titanium alloy in supercritical water containing chloride, phosphate and oxygen

Determining SCC resistance of stainless steel claddings in high- temperature water by constant load crack growth tests and slow strain rate tests

Stress-Corrosion Cracking Sensitization by Hydrogen upon Oxidation of Nickel-base Alloys by Water – an Experiment-Guided First-Principles Study

The correlation between the dislocation slip/grain boundary interaction mode and the resistance to SCC initiation of Alloy 690 in simulated PWR primary water

Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment