Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment
Kai Xi,Wenlong Qi,Yuanfei Li,Yang Zhao,Xiangbing Liu,Tao Zhang,Fuhui Wang
DOI: https://doi.org/10.1016/j.matchar.2024.114445
IF: 4.537
2024-10-17
Materials Characterization
Abstract:This study investigated coupling of thermal aging with irradiation corrosion, and carried out the microstructure and electrochemical characterization of 308 L stainless steel (SS). The passivation performance of 308 L SS was studied under the simulated pressurized water reactor (PWR) environmental condition and its stress corrosion cracking (SCC) performance was tested under thermal aging-irradiation conditions. The experimental results indicate that thermal aging results in spinodal decomposition of δ-ferrite, giving rise to G-phase precipitate and carbide precipitate formation at δ/γ-phase interface, whereas irradiation causes Cr depletion and Ni enrichment at the interface. Both thermal aging and irradiation lead to the decreased corrosion resistance of 308 L SS. Under coupling conditions of the two, severe Cr loss occurs at the phase boundary, which leads to severe corrosion on δ/γ phase boundary and also reduces SCC resistance of 308 L SS.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing