Abstract:Abstract Austenitic stainless steel 316 has very high mechanical properties and corrosion resistance. This type of steel is widely used both in the nuclear and non-nuclear industries. In the nuclear industry, SS316 is used as a cladding material for uranium fuel due to its good corrosion and mechanical properties, and also low neutron absorption cross-section. In the Center for Nuclear Fuel Technology (PTBBN BATAN), it is used as material for the container of nuclear waste that is to be stored on Temporary Storage Installation of Spent Fuel (KHIPSB3 BATAN). SS316 is used as material for can to contain high-activity solid waste from the testing activity in Radiometallurgy Installation (IRM BATAN). The lid of the container is sealed with the GTAW welding process in order to tightly contain the solid waste. The main problem with the heat treatment and welding process of austenitic stainless steel is the occurrence of sensitization in a temperature range of 500-800°C. Therefore fully electrochemical analysis of SS316 stainless steel in various mediums has been conducted. SS 316 specimen was heat-treated to simulate the heat generated by the welding process. Sensitization analysis was conducted with qualitative and quantitative methods by EIS and EPR, and pitting corrosion resistance was by cyclic polarization method. The solution used for EIS and cyclic polarization test was 0 − 3.5% concentration of NaCl, and for EPR test was a mixture of H 2 SO 4 and KSCN. Material characterization before and after corrosion testing was microstructure examination. The result of the corrosion test showed that heat treatment on the temperature range of 500-800°C caused sensitization. The corrosion test curve result showed that a heat treatment temperature of 650°C for 1 hour had the highest activation current. The lowest Rp value for SS316 specimen post heat treatment in 675°C was 69.410 ohm. The welded SS316 specimen had a higher corrosion current than that of the unwelded specimen. The microstructure of the welded specimen showed that there was intergranular corrosion particularly in the HAZ region. The effect of NaCl concentration on the cyclic polarization test showed that the higher the NaCl concentration, the more easily the pitting corrosion. The indication of pitting corrosion occurrence was evaluated by considering the E pit and E rp values. The lower E pit value meant that pitting corrosion was more easily to occur.

Corrosion Behaviour of 316L Stainless Steel in Boric Acid Solutions

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion of 316L exposed to highly concentrated borated water used as shield in nuclear fusion experimental reactors cooling circuits

Behavior of Reinforced Concrete Subjected to Boric Acid Corrosion of Nuclear Power Plant

Noticeable localized corrosion of solid boric acid on 304 stainless steel

Corrosion Mechanisms of 316L Stainless Steel in Polyphosphoric Acid at Elevated Temperature: Behavior and Mechanistic Insights

[Corrosion of Stainless Steel 201, 304 and 316L in the Simulated Sewage Pipes Reactor].

Corrosion of 316L stainless steel in high temperature water and steam: Mechanisms of corrosion

Study on the Behavior and Durability of Reinforced Concrete in Boric Acid Environment

Mechanistic understanding of the localized corrosion behavior of laser powder bed fused 316L stainless steel in pressurized water reactor primary water

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Corrosion Resistance and Passivation Behavior of B-containing S31254 Stainless Steel in a low pH medium

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Electrochemical Corrosion Behaviour of Type 316 Stainless Steel in Acid Media Containing Fluoride Ions

Effect of Temperature and Concentration on the Corrosion Behavior of 42CrMoE Low Alloy Steel in Boric Acid Solution

Effects of Dissolved Gas and Cold Work on the Electrochemical Behaviors of 304 Stainless Steel in Simulated PWR Primary Water

Corrosion of Stainless Steel in Simulated Nuclear Reactor Primary Coolant—Experiments and Modeling

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Corrosion analysis of post-heat treatment and post-weld SS316 with electrokinetic reactivation and cyclic polarization method

A Method for Inhibiting Corrosion of Type 316L Stainless Steel in High-Temperature Molten Chloride Salt

Corrosion Behavior of Ferritic 12Cr ODS and Martensitic X46Cr13 Steels in Nitric Acid and Sodium Chloride Solutions