Effect of boron concentration on microstructures and properties of Fe–B–C alloy steel
Xiangyi Ren,Hanguang Fu,Jiandong Xing,Yongwei Yang,Shuli Tang
DOI: https://doi.org/10.1557/jmr.2017.304
IF: 2.7
2017-01-01
Journal of Materials Research
Abstract:The solidification microstructure, types of eutectic borocarbides, heat treatment properties and wear resistance of steel with x wt% B–0.4 wt% C–6.0 wt% Cr–4.0 wt% Mo–1.0 wt% Al–1.0 wt% Si–1.0 wt% V–0.5 wt% Mn ( x = 1.0, 2.0, 3.0) have been investigated in this present study. The results indicate that the as-cast Fe–B–C alloy steel consists of pearlite, ferrite, and borocarbides M 2 (B,C) (M = Fe, Cr, Mo, V, Mn). After quenching or quenching and tempering treatment, ferrite and pearlite transform into martensite. With the increase of boron content, the macrohardness of alloys increases obviously while wear loss decreases. Borocarbides with chromium addition have good toughness and no cracks are observed on worn surfaces. The wear mechanism changes from micro-cutting accompanied with the spalling of borocarbides to single micro-cutting with the boron content rising.