110 Mw Single-Frequency Yb:YAG Crystal-Derived Silica Fiber Laser at 1064 Nm.

Zhaojun Liu,Yongyao Xie,Zhenhua Cong,Zhigang Zhao,Zhixu Jia,Chengzhi Li,Guanshi Qin,Shang Wang,Xibao Gao,Xianbin Shao,Xingyu Zhang
DOI: https://doi.org/10.1364/ol.44.004307
2019-01-01
Abstract:A single-frequency laser based on Yb:YAG crystal-derived silica fiber (YDSF) was demonstrated. The YDSF was fabricated by a molten-core method with a doping concentration of 4.8 wt. % for Yb2O3, whose gain coeffident and transmission loss were measured to be 1.7 dB/cm and 0.005 dB/cm, respectively. An over 110 mW stable single-frequency laser at 1064 nm was obtained based on a distributed Bragg reflector setup, showing a slope efficiency of 18.5%. The signal-to-noise ratio was similar to 80 dB, and the frequency fluctuation was less than 20 MHz within 10 min. (C) 2019 Optical Society of America