Abstract:Transition metal boride enable applications in fields of cutting tools as the hard phase, but their fabrication suffers from shortcomings in high temperature for binary and hard/soft phase balance. Here, we leveraged a WCoB-Co cermets prepared by using elemental powders of W, Co and B powders via in situ synthesis method and investigated the microstructure evolution of a composite structure of WCoB/Co. The phase evolution, microstructure evolution and mechanical properties were investigated using X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The complete sintering process consist of three solid-phase reaction stages and one liquid-phase sintering stage. The solid-phase reaction stage includes the following three reactions: B + 2Co → Co2B, 11 W +15 Co2B → 9WCoB + W2Co21B6, and 14 W + 2W2Co21B6 → 12WCoB + 23Co + Co7W6. The eutectic liquid phase, essential for the densification, forms at 1323 °C. The Rockwell hardness and density value reach 87.5HRA and 12.11 g/cm3, respectively. At 1380 °C, the traverse rupture strength (TRS) reaches the peak value of 1495 MPa. Moreover, the results show that transgranular fracture is the main fracture mode. The densification stage was completed at ~1400 °C. In particular, Co7W6 phase was discovered during the study of the evolution of WCoB-Co cermets. An increase of the B content was found to be beneficial to eliminate the Co7W6 phase that proved to be detrimental to mechanical properties.

Synthesis and Microstructure Evolution of WCoB Based Cermets During Spark Plasma Sintering

Tracking the evolution of microstructure and phases of WCoB-Co cermets during sintering

Synthesis, microstructure evolution, and phase transformation of novel MoCoB-Co cermets

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Effect of Ni content on the microstructure and properties of WCoB-TiC cermets

Microstructure and mechanical properties of newly synthesized Mo(Co,Fe)B cermets

High-Entropy-Alloy CoFeNiCr Bonded WC-Based Cemented Carbide Prepared by Spark Plasma Sintering

L1 2 strengthening of WC-CoNiFe cemented carbides by spark plasma sintering

Synthesis and characterization of extremely hard and strong (W,Ti,Ta)C cermet by spark plasma sintering

Spark Plasma Sintering of Fine-Grained WC-Co Composites

Single-phase W 2 B 5 ceramic enabled remarkable performance via spark plasma sintering-high-frequency (SPS-HF) process

Effect of chemical composition on the microstructure and mechanical properties of MoCoB based cermets

Dual-grained Mo2FeB2-based cermets containing WC fabricated via multi-step sintering approach: Microstructure, mechanical properties and interface characteristics

Formation of solid solution structures in (Ti,W,Ta,Mo)(C,N) cermet via spark plasma sintering

Fabrication of Hard Cermets by In-Situ Synthesis and Infiltration of Metal Melts into WC Powder Compacts

Microstructure and properties of WC-12Co cemented carbide fabricated via selective electron beam melting

Densification and microstructure evolution of W-TiC-Y2O3 during spark plasma sintering

Effect of Mn addition on the microstructure, interface structure and mechanical properties of MoCoB–Co cermets prepared by in-situ synthesis

Microstructure and mechanical properties of CoCrFeMnNi/WC plasma deposited coating after the spark plasma sintering treatment

Effect of cobalt content on the microstructure, microtexture, and mechanical properties of W-Ni-Fe-xCo alloys during solid-phase-sintering and liquid-phase-sintering