Abstract:Using the traditional preparation method of TiC+TiN powder mixture or simply the Ti(C, N) solid-solution powder to prepare cermet cannot properly avoid the direct contact between TiC, TiN or Ti(C, N) phase and (Co-Ni) binder phase with undesirable wettability, which is disadvantageous to the strength and toughness of cermet. Here, we introduced a new routine using the (Ti, W)(C, N) solid-solution powder and studied the resultant phase constitutions, microstructures and properties of the Ti(C, N)-based cermets, where the cermets prepared with TiC + TiN + WC and Ti(C, N) + WC were taken as counterparts. The X-ray diffraction (XRD) results showed that regardless of the powder combination, two phases, i.e. fcc-(Ti, M)(C, N) and fcc-(Co-Ni), were formed, and the lattice constants of these phases varied in different samples, which is attributed to the specific phase stability (TiN > Ti(C, N) > (Ti, W)(C, N) > TiC) calculated based on the CALPHAD (CALculation of PHAse Diagrams) approach. Transmission electron microscopic (TEM) observations further depicted that besides the already-known core-rim structure, the cermet prepared using (Ti, W)(C, N) uniquely incorporated black-gray rimless grains and black-white-gray rimless grains. Two critical mechanical properties, i.e. hardness (H) and fracture toughness (KIC), were subsequently determined using the Vickers indentation method. It was found that the KIC values of the cermet prepared using (Ti, M)(C, N) were improved by 5.1% ~ 29.2% while maintaining the similar level of H as other cermet samples. The segregation of W and Ti in (Ti, W)(C, N) powders led to the formation of cleavage facets in ceramic grains, which could contribute to the hinderance of crack propagation. Eventually, the high-temperature (750 degrees C) wear tests were conducted to examine the durability of cermet samples. The cermet prepared using (Ti, M)(C, N) generally exhibited enhanced wear resistance, benefiting from the well-balanced H and KIC as well as the restraint of oxidational wear. Thus, this work suggested that preference should be given to (Ti, W)(C, N) solid-solution powders when fabricating high-performance Ti(C, N)based cermets.

Dual-grained Mo2FeB2-based cermets containing WC fabricated via multi-step sintering approach: Microstructure, mechanical properties and interface characteristics

Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Effect of synthetic Mo2FeB2 powder on the microstructure and mechanical properties of Mo2FeB2-based cermets

Interface-reinforced Mo2FeB2-based cermets prepared by multi-step sintering under rapid cooling

Microstructure and mechanical properties of newly synthesized Mo(Co,Fe)B cermets

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Effect of Mo Content on In-Situ Anisometric Grains Growth and Mechanical Properties of Mo2FeB2-Based Cermets

Enhancing mechanical properties of Ti(C, N)-based cermets via preparation with (Ti, W)(C, N) multi-component powder

Microstructure and Properties of Ti(C,N)–Mo2C–Fe Cermets

Sintering Mechanism, Microstructure Evolution and Nanomechanical Properties of Cr-added Mo2FeB2 Based Cermets

Microstructure and Mechanical Properties of Mo 2 FeB 2 Based Cermets with/without Nb Addition

Microstructure, mechanical properties, and corrosion resistance of Mo2(Fe,Ni)B2-based cermets prepared by reaction boronizing sintering

On the dissolution and enhancement mechanisms of Cr doping in Mo2FeB2-based cermets

Ultrafine (Ti, M)(C, N)-based cermets with optimal mechanical properties

Effect of Mo/B Atomic Ratio on the Microstructure and Mechanical Properties of Mo2FeB2 Based Cermets

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

The Fabrication of Multi-Core Structure Cermets Based on (ti,w,ta)cn and Ticn Solid-Solution Powders

Synthesis, microstructure evolution, and phase transformation of novel MoCoB-Co cermets

Effect of (Ti, W, Mo, V)(C, N) powder size on microstructure and properties of (Ti, W, Mo, V)(C, N)-based cermets

Effect of Mo2C Addition on the Formation of Core-Rim Structure and Mechanical Properties of Ti(C,N)-WC-Mo2C-(Ni, Co) Cermet

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature