Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Hao Wu,Yong Zheng,Jiajie Zhang,Zheng Ke,Xiangyu Xu

DOI: https://doi.org/10.1016/j.ceramint.2021.04.065

IF: 5.532

2021-07-01

Ceramics International

Abstract:<p>Herein, Mo₂FeB₂-based cermets, with nominal composition of Mo₂FeB₂-2.06Fe-2.9Ni-2.5Cr-<em>x</em>WC-0.04C (<em>x</em> = 0, 2.5, 5, 10 wt %), are fabricated by multi-step sintering to investigate influence of tungsten carbide (WC) content on microstructure and mechanical properties. Results reveal that the microstructure of WC-free cermets resembles that of traditional cermets. However, microstructure of WC-containing cermets (<em>x</em> = 2.5 wt %) is composed of fine black core/grey rim Mo₂FeB₂ grains and coarse white-colored coreless Fe₃(W,Mo)₃C grains. Furthermore, at <em>x</em> ≥ 5 wt %, most of white coreless Fe₃(W,Mo)₃C grains are transformed into a white core/black rim structure. From these observations, it can be concluded that growth of nearly round-shaped Mo₂FeB₂ grains is through diffusion-control, leading to normal grain growth (NGG), whereas the growth of polyhedral Fe₃(W,Mo)₃C grains is dictated by the interfacial reactions, resulting in 2D nucleation and partially abnormal grain growth (AGG). In addition, grain size distribution of WC-containing cermets exhibits distinct bimodal characteristics, where average grain size is smaller than that of WC-free cermets. More importantly, presence of WC significantly improves the mechanical properties, resulting in superior fracture toughness of 25.1 ± 0.5 MPa m^1/2 and hardness of 90.3 ± 0.1 HRA, at <em>x</em> = 5 wt %, without compromising much of transverse rupture strength.</p>

materials science, ceramics