Abstract:Herein, Mo2FeB2-based cermets, with nominal composition of Mo2FeB2-2.06Fe-2.9Ni-2.5Cr-xWC-0.04C (x = 0, 2.5, 5, 10 wt %), are fabricated by multi-step sintering to investigate influence of tungsten carbide (WC) content on microstructure and mechanical properties. Results reveal that the microstructure of WC-free cermets resembles that of traditional cermets. However, microstructure of WC-containing cermets (x = 2.5 wt %) is composed of fine black core/grey rim Mo2FeB2 grains and coarse white-colored coreless Fe3(W,Mo)3C grains. Furthermore, at x ≥ 5 wt %, most of white coreless Fe3(W,Mo)3C grains are transformed into a white core/black rim structure. From these observations, it can be concluded that growth of nearly round-shaped Mo2FeB2 grains is through diffusion-control, leading to normal grain growth (NGG), whereas the growth of polyhedral Fe3(W,Mo)3C grains is dictated by the interfacial reactions, resulting in 2D nucleation and partially abnormal grain growth (AGG). In addition, grain size distribution of WC-containing cermets exhibits distinct bimodal characteristics, where average grain size is smaller than that of WC-free cermets. More importantly, presence of WC significantly improves the mechanical properties, resulting in superior fracture toughness of 25.1 ± 0.5 MPa m1/2 and hardness of 90.3 ± 0.1 HRA, at x = 5 wt %, without compromising much of transverse rupture strength.

Interface-reinforced Mo2FeB2-based cermets prepared by multi-step sintering under rapid cooling

Dual-grained Mo2FeB2-based cermets containing WC fabricated via multi-step sintering approach: Microstructure, mechanical properties and interface characteristics

Microstructure and mechanical properties of newly synthesized Mo(Co,Fe)B cermets

Effect of synthetic Mo2FeB2 powder on the microstructure and mechanical properties of Mo2FeB2-based cermets

Microstructure, mechanical properties, and corrosion resistance of Mo2(Fe,Ni)B2-based cermets prepared by reaction boronizing sintering

Sintering Mechanism, Microstructure Evolution and Nanomechanical Properties of Cr-added Mo2FeB2 Based Cermets

Effect of Mo Content on In-Situ Anisometric Grains Growth and Mechanical Properties of Mo2FeB2-Based Cermets

On the dissolution and enhancement mechanisms of Cr doping in Mo2FeB2-based cermets

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Synthesis, microstructure evolution, and phase transformation of novel MoCoB-Co cermets

Microstructure and Mechanical Properties of Mo 2 FeB 2 Based Cermets with/without Nb Addition

Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Synthesis and characterization of Mo@Ni core-shell composite powder-reinforced (W,Ti)C-based cermet

Growth kinetics of ceramic grains during liquid phase sintering in Mo2FeB2-based cermets

Effect of Milling Time on the Microstructure and Mechanical Properties of Mo2FeB2 Based Cermets

Ultrafast high-temperature sintering to avoid metal loss toward high-performance and scalable cermets

Bulk Mo2FeB2 Based Cermets Fabricated by Mechanical Ball Milling and Reaction Boronizing Sintering

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

On the reaction mechanism of Mo2FeB2-based cermets and wear transition induced by self-lubricating tribo-oxide layer

Experimental Investigation and Thermodynamic Analysis of TiC–Fe Cermets with Mo Additions

The Formation of Ni-Mo Alloy Phase in Ticn-Based Cermets