Abstract:In a previous study, we presented a novel manufacturing process for the creation of 6 × 6 and 8 × 8 microlens arrays (MLAs) comprising lenses with diameters of 1000 μm, 500 μm, and 200 μm within an area that covers 10 mm × 10 mm. In the current study, we revised the manufacturing process to allow for the fabrication of MLAs of far higher density (15 × 15 and 29 × 29 within the same area). In this paper, we detail the revised manufacturing scheme, including the micromachining of molds, the partial-curing polydimethylsiloxane (PDMS) bonding used to fuse the glass substrate and PDMS, and the multi-step casting process. The primary challenges that are involved in creating MLAs of this density were ensuring uniform membrane thickness and preventing leakage between the PDMS and glass substrate. The experiment results demonstrated that the revised fabrication process is capable of producing high density arrays: Design I produced 15 × 15 MLAs with lens diameter of 0.5 mm and fill factor of 47.94%, while Design II produced 29 × 29 MLAs with lens diameter of 0.25 mm and fill factor of 40.87%. The partial-curing PDMS bonding system also proved to be effective in fusing PDMS with glass (maximum bonding strength of approximately six bars). Finally, the redesigned mold was used to create PDMS membranes of high thickness uniformity (coefficient of variance <0.07) and microlenses of high lens height uniformity (coefficient of variance <0.15).

Fabrication of Ternary Ge–Se–Sb Chalcogenide Microlens Arrays Using Thermal Reflow

Transmission of refractive microlens array by reactive ion beam etching

Step heat-forming photoresist method for expanding the N. A. range of refractive microlens

Fabrication of Chalcogenide Glass Based Hexagonal Gapless Microlens Arrays via Combining Femtosecond Laser Assist Chemical Etching and Precision Glass Molding Processes

Fabrication of microlens array on chalcogenide glass by wet etching-assisted femtosecond laser direct writing

Fabrication of multi-focal chalcogenide glass microlens arrays based on femtosecond laser-assisted chemical etching method

Rib and strip chalcogenide waveguides based on Ge-Sb-Se radio-frequency sputtered films

Fabrication of Large-Area Silicon Spherical Microlens Arrays by Thermal Reflow and ICP Etching

An Ultraviolet-Lithography-Assisted Sintering Method for Glass Microlens Array Fabrication

Micro Aspheric Glass Lens Molding Process

Fabrication Of Chalcogenide Microlens Array Using Hot Embossing Method

Demonstration of High-Performance, Sub-Micron Chalcogenide Glass Photonic Devices by Thermal Nanoimprint

Thermal mechanism-driven microlens formation in Ge–Sb–S glasses by direct laser writing: composition dependent insight

One-step Fabrication of Achromatic Spherical Microlens Array on Enzyme Etched Gelatin Film

Experimental study of the fabrication of chalcogenide glass lenses by using precision glass molding

Fabrication of a double-sided micro-lens array by a glass molding technique

Femtosecond laser writing of infrared microlens arrays on chalcogenide glass

Chalcogenide microlens arrays fabricated using hot embossing with soft PDMS stamps

Reactive ion etching of Ge-Sb-Se ternary chalcogenide glass films in fluorine plasma

Microlens arrays prepared via colloidal crystal templating

Using Micromachined Molds, Partial-curing PDMS Bonding Technique, and Multiple Casting to Create Hybrid Microfluidic Chip for Microlens Array