Abstract:The AlN/BN composite ceramic, fabricated via hot-press sintering, exhibits obvious anisotropy due to the establishment of directional alignment of h-BN. However, the variation and influence mechanisms of bending strength (σ) and thermal conductivity (λ) are remain unclear in different directions, which greatly limit the application of AlN/BN composite ceramics. In this paper, the effects of h-BN content on phase composition, microstructure and anisotropy of AlN/BN composite ceramics are discussed in detail. The results reveal that AlN/BN composite ceramics have three directions: perpendicular (⊥), longitudinal parallel (∥), and lateral parallel (≡) to the hot-pressing direction. The content of h-BN is a crucial factor affecting the anisotropy of AlN/BN composite ceramics. h-BN enhances the thermal conductivity in the ∥ and hinders the thermal conductivity in the ⊥. With the increase in h-BN amount, λ∥ rises gradually, while λ⊥ gradually falls. When the mass percentage of h-BN and AlN is 25 % (AB25), the λ∥ is as high as 90 W m−1 K−1, which is about 2.25 times that of λ⊥. In terms of mechanical properties, σ ≡ and σ ⊥ first increase and then decrease, while σ ∥ only decreases. This is attributable to h-BN being effective in enhancing mechanical properties by inhibiting crack propagation in the ⊥ and ≡ direction, while the promotion of crack propagation leads to a decrease in mechanical properties in the ∥ direction. σ ≡ reaches the highest values (σ ≡ = 460.2 MPa) at an h-BN amount of 10 % (AB10), which is about 1.19 and 2.04 times that of σ ⊥ and σ ∥, respectively, and 22.1 % higher than that of AB0.

Thermal properties and thermal shock resistance of BAS-BN composite ceramics

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Hot-press sintering studies of sol-gel-prepared composite powders: A novel preparation method to improve mechanical properties of BN-BAS composite ceramics

Improved thermal shock and oxidation resistance of β-SiAlON incorporated with h-BN

Microstructural evolution of h-BN matrix composite ceramics with La-Al-Si-O glass phase during hot-pressed sintering

Effect of hexagonal boron nitride content on the anisotropy of hot-press-sintered AlN/BN composite ceramics

Anisotropies in structure and properties of hot-press sintered h-BN-MAS composite ceramics: Effects of raw h-BN particle size

EFFECT OF h-BN AS AN ADDITIVE ON PHYSICAL AND MECHANICAL PROPERTIES OF Al2TiO5 COMPOSITE

Microstructural evolution and mechanical properties of h-BN composite ceramics with Y2O3–AlN addition by liquid-phase sintering

Effects of h-BN addition on microstructures and mechanical properties of β-CaSiO3 bioceramics

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Thermal Shock Behavior of Si3N4/BN Fibrous Monolithic Ceramics

Influence of sintering temperature on the crystallization and mechanical properties of BN‐MAS composites