Irradiation Effects on Amosic-3 Silicon Carbide Composites by Si Ions Implantation
Yahuan Zhao,Xiaoqiang Li,Chuanxin Liu,Hong Yang,Bo Chen,Yiming Qin,Shanshan Xu,Laifei Cheng,Litong Zhang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.07.014
IF: 5.7
2019-01-01
Journal of the European Ceramic Society
Abstract:SiCf/SiC composites were irradiated to over 100 dpa with 300 keV Si ions at 300 degrees C. Here, electron microscopy and Raman spectroscopy were utilized to study the microstructural evolution. The Raman spectra of fiber and matrix showed that the crystal structure was seriously damaged. TEM images revealed that the fiber underwent grain nucleation and growth in lower fluence region, accompanied by an amorphous layer near the damage peak area. Also, the matrix went through recrystallization, and the columnar grains turned into equiaxial ones. Moreover, stacking faults and massive amorphous islands were observed in high resolution TEM images. Following irradiation at 300 degrees C, the matrix swelled, but the fiber and interphase shrunken along the axis. And, more remarkably, the hardness of fiber and matrix decreased to different extents, a result that was explained by the generation of amorphous islands and breakdown of covalent bonds, and recrystallization might be responsible for this.