Abstract:The formation possibility of a new (Zr0.25Nb0.25Ti0.25V0.25)C high-entropy ceramic (ZHC-1) was first analyzed by the first-principles calculations and thermodynamical analysis and then it was successfully fabricated by hot pressing sintering technique. The first-principles calculation results showed that the mixing enthalpy of ZHC-1 was 5.526 kJ/mol and the mixing entropy of ZHC-1 was in the range of 0.693R-1.040R. The thermodynamical analysis results showed that ZHC-1 was thermodynamically stable above 959 K owing to its negative mixing Gibbs free energy. The experimental results showed that the as-prepared ZHC-1 (95.1% relative density) possessed a single rock-salt crystal structure, some interesting nanoplate-like structures and high compositional uniformity from nanoscale to microscale. By taking advantage of these unique features, compared with the initial metal carbides (ZrC, NbC, TiC and VC), it showed a relatively low thermal conductivity of 15.3 + - 0.3 W/(m.K) at room temperature, which was due to the presence of solid solution effects, nanoplates and porosity. Meanwhile, it exhibited the relatively high nanohardness of 30.3 + - 0.7 GPa and elastic modulus of 460.4 + - 19.2 GPa and the higher fracture toughness of 4.7 + - 0.5 MPa.m1/2, which were attributed to the solid solution strengthening mechanism and nanoplate pullout and microcrack deflection toughening mechanism.

Synthesis and Characterization of (zr1/3nb1/3ti1/3)c Metal Carbide Solid-Solution Ceramic

In Situ Reaction and Solid Solution Induced Hardening in (Ti,zr)b2-(Zr,ti)c Composites

First-principles Study, Fabrication and Characterization of (zr0.25nb0.25ti0.25v0.25)c High-Entropy Ceramics

First-principles study, fabrication and characterization of (Zr0.25Nb0.25Ti0.25V0.25)C high-entropy ceramic

Novel TiC-based ceramic with enhanced mechanical properties by reaction hot-pressing at low temperature

In situ reaction and solid solution induced hardening in (Ti,Zr)B 2 ‐(Zr,Ti)C composites

Densification, Microstructures, and Mechanical Properties of (zr, Ti)(C, N) Ceramics Fabricated by Spark Plasma Sintering

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Novel TiC-based composites with enhanced mechanical properties

First-principles Study, Fabrication, and Characterization of (hf0.2zr0.2ta0.2nb0.2ti0.2)c High-Entropy Ceramic

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

The influence of Ti-induced precipitates on the microstructure and mechanical properties of (Zr,W)C solid solution

Novel (Zr, Ti)(C, N)–SiC ceramics via reactive hot-pressing at low temperature

Synthesis, Mechanical and Physical Properties of Bulk Zr2Al4C5 Ceramic

Synthesis of the Ternary Metal Carbide Solid‐solution Ceramics by Polymer‐derived‐ceramic Route

Host Lattice and Solid Solution Formation in an Octal-Cation (NbTaZrTiHfVWMo)C High Entropy Carbide Ceramic

Densification, Microstructure and Mechanical Properties of Multicomponent (tizrhfnbtamo)c Ceramic Prepared by Pressureless Sintering

Addition Effect of ZrC Nano-powder on the Microstructure and Mechanical Properties of TiCN-based Cermets Prepared by Spark Plasma Sintering

Understanding the electronic structure, mechanical properties, and thermodynamic stability of (TiZrHfNbTa)C combined experiments and first-principles simulation

Microstructure and Mechanical Properties of (tizrnbtamo)c High-Entropy Ceramic

Preparation and Mechanical Properties of (TiCrZrNb)C4-SiC Multiphase High-Entropy Ceramics