Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Synthesis, Mechanical and Physical Properties of Bulk Zr2Al4C5 Ceramic

Synthesis and Mechanical Properties of High-Purity Cr2alc Ceramic

Microstructure and mechanical properties of Zr3Al3C5-based ceramics synthesized by Al-Si melt infiltration

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Mechanical Properties of ZrB<sub>2</sub>-Based Ceramics Reinforced by Nano-SiC Whiskers

Sintering Behavior and Mechanical Properties of Alumina-Coated Zirconia Ceramics

Thermal Stability of Bulk Zr2Al4C5 Ceramic at Elevated Temperatures

Thermal and Electrical Transport in ZrB2-SiC-WC Ceramics Up to 1800 °C

In Situ ZrB2 Formation in B4C Ceramics and Its Strengthening Mechanism on Mechanical Properties

Novel TiC-based ceramic with enhanced mechanical properties by reaction hot-pressing at low temperature

In Situ Reaction Synthesis And Mechanical Properties Of V2alc

Mechanical and Thermal Properties of Antiperovskite Ti3alc Prepared by an in Situ Reaction/Hot-Pressing Route

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Reaction Behavior, Microstructure, and Radiative Properties of In Situ ZrB 2 -SiC Ceramic Composites from a Si-Zr-B 4 C System