Abstract:The synthesis of the multi-component transition-metal diboride (MeB2) solid-solution powders has been recently attracting considerable attentions. However, the synthesis of the ternary or more component MeB2 solid-solution powders has rarely been reported until now. To fabricate the ternary MeB2 solid-solution powders, herein we utilized two kinds of the ternary MeB2 solid solutions as prototypes, namely (Hf1/3Zr1/3Ti1/3)B-2 (HZTB) and (Ta1/3Nb1/3Ti1/3)B-2 (TNTB). The formation possibility of HZTB and TNTB was first analyzed by the first-principles calculations and then we attempted of fabricated them by a simple molten salt synthesis technique. The first-principles calculations results showed that the mixing Gibbs free energy at room temperature and lattice size difference at 0 K of HZTB and TNTB were (1.666 kJ/mol and 3.146%) and (-3.030 kJ/mol and 1.254%), respectively. This suggested that TNTB solid solution was more prone to being fabricated than HZTB solid solution. The experimental results showed the high purity TNTB solid-solution nanopowders were successfully synthesized by the molten salt synthesis technique at 1373 K with 30% excessive B as precursors while the HZTB solid solution was not able to be synthesized by the molten salt synthesis technique. The as-synthesized TNTB solid-solution nanopowders exhibited the distinguished nanorod morphology with the diameters of 20-40 nm and lengths of 100-200 nm. Meanwhile, they possessed the good single-crystal hexagonal structure and high compositional uniformity from nanoscale to microscale. In addition, their formation mechanism associated to the possible chemical reactions was well interpreted by the thermodynamics analysis.

Synthesis of the Ternary Metal Carbide Solid‐solution Ceramics by Polymer‐derived‐ceramic Route

Novel Synthesis of (hf 0.25 Zr 0.25 Ti 0.25 Ta 0.25 )C-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Synthesis and Characterization of (zr1/3nb1/3ti1/3)c Metal Carbide Solid-Solution Ceramic

Fabrication and Characterization of Polymer‐derived High‐entropy Carbide Ceramic Powders

Structure evolutions of the polymer derived medium-/high-entropy metal carbides

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Synthesis of Metastable Ternary Pd-W and Pd-Mo Transition Metal Carbide Nanomaterials

A New Route to Fabricate Dual-Phase Compositionally Complex Ceramics

Microstructure and EMW absorption properties of PDCs-SiCN(Ti) ceramics with adjustable SiC nanowires and TiC nanocrystallines

Preparation of (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C high‐entropy ceramic nanopowders via liquid‐phase precursor

Synthesis and Characterization of the Ternary Metal Diboride Solid‐solution Nanopowders

One‐step Synthesis of Coral‐like High‐entropy Metal Carbide Powders

Synthesis of TaB 2 -TaC nanocomposite powders by a boro-carbothermal reduction route

Effect of pre-solid solution treatment of secondary carbides on the microstructure and mechanical properties of Ti(C,N)-based cermets

Host Lattice and Solid Solution Formation in an Octal-Cation (NbTaZrTiHfVWMo)C High Entropy Carbide Ceramic

Powder synthesis, densification, microstructure and mechanical properties of Hf-based ternary boride ceramics

Ta(B, C, N) and (ta, Mi)(B, C, N) (mi = Nb, W) Ceramics by High‐energy Ball Milling: Processing and Solution Mechanisms

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Densification, Microstructures, and Mechanical Properties of (zr, Ti)(C, N) Ceramics Fabricated by Spark Plasma Sintering

Preparation of high-performance (ZrHfTaNbTiMo)C–10Co ceramic by SPS using self-synthesized fine high-entropy carbide powders

Phase Transition of Multi-Component (tizrvnb)c Ceramics—part I: Phase Decomposition Induced by Carbon Content