Abstract:Abstract Because of the excellent fracture toughness and oxidation resistance, carbon short fiber reinforced ceramics have a sound potential for a variety of high‐temperature applications. For the composite's reliable use in long‐term applications, however, the oxidation effects on the mechanical strength are of crucial interest and have hitherto not been investigated in detail yet. In this study, the weight change of carbon short fiber reinforced C/SiC composites with carbon fiber lengths of 9 mm (long cut fiber composite – LCFC) and 2 mm (short milled fiber composite – SMFC), respectively, are evaluated in the temperature range from 500 to 1200 °C for two different fiber orientations. Both types of composites were additionally tested in bending mode after 25 and 50 min of exposure to air at 700 °C depending on fiber orientation. After 3 h of exposure at 1000 °C, a total weight loss of up to 37% for LCFC and 47% for SMFC could be determined. The bending test carried out after 50 min exposure at 700 °C showed a dramatic decrease down to 50% of the initial flexural strength for LCFC samples with fibers orientated in parallel to the beam axis. The smallest strength decrease of around 13% was found for SMFC samples with fibers orientated perpendicularly to the beam axis. Microstructural investigations suggest strongly that oxidation along the fibers is the most dominating weakening mechanism and is therefore directly affected by the fiber orientation and length.

Oxidation Behavior Of A 2d-Sicf/Bn/Sibcn Composite At 1350-1650 Degrees C In Air

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Microstructural evolution and oxide layer structure of Csf/SiBCN composites during oxidation at 1500 °C

Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100°C

Wet oxidation behavior of C/SiC–SiHf(B)CN composites at high temperature

Long-term oxidation resistant SiC/SiC-SiHfBCN composites: A promising thermo-structural material aims for hypersonic roundtrip

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Oxidation of SiC/BN/SiC ceramic matrix composites in dry and wet oxygen at intermediate temperatures

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

Long‐term oxidation and ablation behavior of Cf/ZrB2–SiC composites at 1500, 2000, and 2200°C

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Oxidation mechanism of Al–Si–SiC composite at elevated temperature

Oxidation behavior of 3D Hi–Nicalon/SiC composite

Effects of pyrolysis temperatures on the oxidation behavior of PIP-processed SiCf/SiC composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Thermal Protection and Dielectric Properties of Borosilicate Coatings for SiCf/SiC Composites Under High-Temperature Oxidation