Abstract:In this study, the microstructural changes in irradiated W-1 wt%Pr2O3, W-1 wt%La2O3, W-1 wt%TiC and W-1 wt%ZrC specimens by 1 MeV Fe+ ion irradiation to doses of 1 dpa at room temperature have been characterized by transmission electron microscopy (TEM) to understand the radiation damage. The specimens of 1 dpa were consecutively annealed at temperatures of 600 degrees C, 800 degrees C, 900 degrees C and 1100 degrees C for 1h, and the post-irradiation annealing effect on the microstructure was studied. Microstructural features such as dislocations, dislocation loops and dense dislocation networks were observed by the means of TEM. There was a significant change in the microstructure of the tungsten (W) after irradiation and post-irradiation annealing. W-1 wt%TiC likely consisted of fewer radiation-induced defects and hence exhibits higher resistance to radiation-induced microstructural changes than the others. The general trend is that the density of defect clusters decreases while the average size of the clusters increases with the annealing temperature. A complete removal of dislocation structures at 1100 degrees C occurred in all materials. The irradiation damage effect of Fe+ ions on the deuterium retention of as-synthesized W-based composites was investigated. Thermal desorption spectroscopy of W implanted with D-2 (-) ions was performed using the low-energy ion irradiation system of Kyoto University. Compared with the samples without Fe preirradiation, the deuterium retention of the four composites increased after Fe+ pre-irradiation. The retained amount of deuterium was also increased with the increase in the Fe+ irradiation dose. This is of vital importance to the scientific community working on these materials for extreme irradiating environments.

Investigation of microstructure and irradiation behavior of W–Nb/Ti composites prepared by spark plasma sintering

Effect of Doped Niobium on the Microstructure and Properties of W–Nb/TiC Composites Prepared by Spark Plasma Sintering

Microstructure and Properties of TiN-reinforced W–Ti Alloys Prepared by Spark Plasma Sintering

Microstructure, densification and mechanical properties of in situ TiBw/Ti2AlNb composites fabricated by spark plasma sintering

Investigation on microstructure and reinforcement mechanism of the TiC-reinforced W-matrix composite prepared by high-energy ball milling and spark plasma sintering

Influence of TiN nanoparticles on the microstructure and properties of W matrix materials prepared by spark plasma sintering

Microstructure and Transient Laser Thermal Shock Behavior of W–TiC–Y2O3 Composites Prepared by Wet Chemical Method

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Microstructure and deuterium retention after ion irradiation of W–Lu2O3 composites

Study on the Microstructure and Mechanical Properties of W-wire/TiBe, ZrBe, and ZrTiBe Alloy Composites

Microstructure and Performances of W–TiC–Y2O3 Composites Prepared by Mechano-Chemical and Wet-Chemical Methods

Microstructure evolution of Ti64-TiBw composites via electron beam powder bed fusion using as-prepared composite powder as feedstock

Preparation of TiC-doped W-Ti Alloy and Heat Flux Performance Test under Laser Beam Facility

Microstructural Effects of Y2O3 and TiC Additions in Tungsten

TiB Whisker and Nitrogen Solid‐Solution Synergistic‐Strengthened Titanium Matrix Composites by Ti–BN via Spark Plasma Sintering and Hot Extrusion

Microstructures and Properties of W-Lu2O3 Composites Strengthened with Nb and C Trace Elements

Microstructure Evolutions of the W–TiC Composite Conducted by Dual-Effects from Thermal Shock and He-ion Irradiation

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF (Nb,Ti)C-Ni COMPOSITE

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

TEM Studies of 1 MeV Fe+ Ion-Irradiated W Alloys by Wet Chemical Method: High-Temperature Annealing and Deuterium Retention

Effects of Zirconium Element on the Microstructure and Deuterium Retention of W–Zr/Sc2O3 Composites