Abstract:Highly ordered mesoporous silicon carbide ceramics have been successfully synthesized with yields higher than 75% via a one-step nanocasting process using commercial polycarbosilane (PCS) as a precursor and mesoporous silica as hard templates. Mesoporous SiC nanowires in two-dimensional (2D) hexagonal arrays (p6m) can be easily replicated from a mesoporous silica SBA-15 template. Small-angle X-ray diffraction (XRD) patterns and transmission electron microscopy (TEM) images show that the SiC nanowires have long-range regularity over large areas because of the interwire pillar connections. A three-dimensional (3D) bicontinuous cubic mesoporous SiC structure (Ja3d) can be fabricated using mesoporous silica KIT-6 as the mother template. The structure shows higher thermal stability than the 2D hexagonal mesoporous SiC, mostly because of the 3D network connections. The major constituent of the products is SiC, with 12% excess carbon and 14% oxygen measured by elemental analysis. The obtained mesoporous SiC ceramics are amorphous below 1200 degrees C and are mainly composed of randomly oriented beta-SiC crystallites after treatment at 1400 degrees C. N-2-sorption isotherms reveal that these ordered mesoporous SiC ceramics have high Brunauer-Emmett-Teller (BET) specific surface areas (up to 720 m(2) g(-1)), large pore volumes (similar to 0.8 cm(3) g(-1)), and narrow pore-size distributions (mean values of 2.0-3.7 nm), even upon calcination at temperatures as high as 1400 degrees C. The rough Surface and high order of the nanowire arrays result from the strong interconnections of the SiC products and are the main reasons for such high surface areas. XRD, N-2-sorption, and TEM measurements show that the mesoporous SiC ceramics have ultrahigh stability even after re-treatment at 1400 degrees C under a N-2 atmosphere. Compared with 2D hexagonal SiC nanowire arrays, 3D cubic mesoporous SiC Shows superior thermal stability, as well as higher surface areas (590 m(2) g(-1)) and larger pore volumes (similar to 0.71 cm(3) g(-1)).

Low-Temperature Synthesis of Mesoporous Sic Hollow Spheres by Magnesiothermic Reduction

Low-temperature pseudomorphic transformation of ordered hierarchical macro-mesoporous SiO2/C nanocomposite to SiC via magnesiothermic reduction.

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Preparation of Mesoporous Si Nanoparticles by Magnesiothermic Reduction for the Enhanced Reactivity

High-Surface-Area Zeolitic Silica with Mesoporosity

Low temperature strategy to synthesize high surface area mesoporous hydroxypropyl-β-cyclodextrin-based silicas via benign template removal

The Synthesis Of Mesoporous Molecular Sieves

Facile mesoporous template-assisted hydrothermal synthesis of ordered mesoporous magnesium silicate as an efficient adsorbent

Manipulation Of Phase And Microstructure At Nanoscale For Sic In Molten Salt Synthesis

Self‐templated magnesiothermic reduction of ORMOSIL particles to monodisperse hollow spherical SiC composite particles

Facile fabrication of three-dimensional mesoporous Si/SiC composites via one-step magnesiothermic reduction at relative low temperature

A Facile Soft-Template Synthesis of Mesoporous Polymeric and Carbonaceous Nanospheres

Salt-templated Synthesis and Morphological Control of Monodisperse Hollow Mesoporous Structures

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

Ultralow Temperature Synthesis of Ordered Hexagonal Smaller Supermicroporous Silica Using Semifluorinated Surfactants As Template.

Direct Preparation of Hierarchical Macroporous Β-Sic Using SiO2 Opal As Both Template and Precursor and Its Application in Water Splitting

High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template

Hierarchically macro/mesoporous silica monoliths constructed with interconnecting micrometer-sized unit rods

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Highly Ordered Mesoporous Silicon Carbide Ceramics with Large Surface Areas and High Stability