Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Low temperature strategy to synthesize high surface area mesoporous hydroxypropyl-β-cyclodextrin-based silicas via benign template removal

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

High temperature synthesis of hydrothermally stable micro-mesoporous silica and Al-doped mesoporous silica via rigid template

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Template-free Hydrothermal Preparation of Mesoporous TiO2 Microspheres on a Large Scale

A mild method to remove organic templates in periodic mesoporous organosilicas by the oxidation of perchlorates

Ultralow Temperature Synthesis of Ordered Hexagonal Smaller Supermicroporous Silica Using Semifluorinated Surfactants As Template.

Controllable Preparation Of Ultra-Low-Dielectric Nanoporous Silica Via Inorganic-Organic Hybrid Templates

Preparation of Nano-Sized Mesoporous Silica Dioxide and Al-Doped Silica Dioxide at Extremely Low Reactant Concentration

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Low-cost route for synthesis of mesoporous silica materials with high silanol groups and their application for Cu(II) removal

Direct synthesis of hydrothermally stable micro–mesoporous silicas templated by unsaturated α-linolenic acid self-assemblies under high temperature hydrothermal conditions

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

A novel low temperature vapor phase hydrolysis method for the production of nano-structured silica materials using silicon tetrachloride

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

Simultaneous Removal of Copolymer Template from SBA-15 in the Crystallization Process

Low-Temperature Strategy To Synthesize Highly Ordered Mesoporous Silicas With Very Large Pores

Synthesis of mesoporous silica using CO2/N2switchable surfactant as soft templates

A Facile Preparation of Transparent and Monolithic Mesoporous Silica Materials

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media