Abstract:Highly ordered hexagonal mesoporous silica materials (JLU-20) with uniform pore sizes have been successfully synthesized at high temperature (150-220degreesC) by using fluorocarbon-hydrocarbon surfactant mixtures. The fluorocarbon-hydrocarbon surfactant mixtures combine the advantages of both stable fluorocarbon surfactants and ordered hydrocarbon surfactants, giving ordered and stable mixed micelles at high temperature (150-220degreesC). Mesoporous JLU-20 shows extraordinary stability towards hydrothermal treatment (100% steam at 800degreesC for 2 h or boiling water for 80 h), thermal treatment (calcination at 1000degreesC for 4 h), and toward mechanical treatment (compressed at 740 MPa). Transmission electron microscopy images of JLU-20 show well-ordered hexagonal arrays of mesopores with one-dimensional (M) channels and further confirm that JLU-20 has a two-dimensional (2D) hexagonal (P6mm) mesostructure. Si-29 HR MAS NMR spectra of as-synthesized JLU-20 shows that JLU-20 is primarily made up of fully condensed Q(4) silica units (delta = - 112 ppm) with a small contribution from incompletely cross-linked Q(3) (delta = - 102 ppm) as deduced from the very high Q(4)/Q(3) ratio of 6.5, indicating that the mesoporous walls of JLU-20 are fully condensed. Such unique structural features should be directly attributed to the high-temperature synthesis, which is responsible for the observed high thermal, hydrothermal, and mechanical stability of the mesoporous silica materials with well-ordered hexagonal symmetry. Furthermore, the concept of "high-temperature-synthesis" is successfully extended to the preparation of three-dimensional (3D) cubic mesoporous silica materials by the assistance of a fluorocarbon surfactant as a co-template. The obtained material, designated JLU-21, has a well-ordered cubic Im3m mesostructure with fully condensed pore walls and shows unusually high hydrothermal stability, as compared with conventional cubic mesoporous silica materials such as SBA-16.

High temperature synthesis of hydrothermally stable micro-mesoporous silica and Al-doped mesoporous silica via rigid template

Direct synthesis of hydrothermally stable micro–mesoporous silicas templated by unsaturated α-linolenic acid self-assemblies under high temperature hydrothermal conditions

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Synthesis of Highly Ordered and Hydrothermally Stable Mesoporous Materials Using Sodium Silicate As a Precursor

High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

Fabricating Mesoporous Silica-Modified Alumina with High Thermal Stability

High-Temperature Synthesis and Formation Mechanism of Stable, Ordered Mcm-41 Silicas by Using Surfactant Cetyltrimethylammonium Tosylate As Template

A novel mesoporous silica-clay composite and its thermal and hydrothermal stabilities

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieves with High Stability in High-Temperature Steam

Synthesis of hydrothermally stable, hierarchically mesoporous aluminosilicate Al-SBA-1 and their catalytic properties

High-temperature synthesis of stable ordered mesoporous silica materials by using fluorocarbon-hydrocarbon surfactant mixtures.

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Highly hydrothermal stability of ordered mesoporous aluminosilicates Al-SBA-15 with high Si/Al ratio

The Synthesis and Hydrothermal Stability Test of Mesoporous Molecular Sieve with Micropores

Hydrothermal Transformation and Characterization of Porous Silica Templated by Surfactants

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure