Abstract:The hydrothermal stability of ordered mesoporous aluminosilicate (Al-SBA-15) materials was systematically investigated under 100% steam at high temperature (600 – 800°C). The characterization results clearly indicate that the incorporation of a little amount of aluminum in the framework, large amount of micropores and high calcination temperature can greatly improve the hydrothermal stability of mesoporous silicate materials. The two-dimensional (2-D) hexagonal mesostructure of the Al-SBA-15 materials calcined at 600°C can be stable in the steam of 600°C for more than 12h. However, the mesostructures of Al-SBA-15 materials with a relatively low Si/Al ratio (molar ratios in the initial solution) of 10–30 completely collapse under the steam of 800°C, but the samples with less Al content (a high Si/Al ratio of 40–50) are much stable and can withstand for 6h in the 800°C-steam. It is due to the presence of large amount of micropores and the formation of more stable Si–O–Al bonds on the surface of the frameworks. By elevating the calcination temperature to 800°C, the polymerization degree of the frameworks is enhanced, and they can withstand the steam treatment of 800°C for more than 12h. In addition, it is observed that the mesoporous aluminosilicates (Al-SBA-15) are hydrothermally more stable than of the pristine silica SBA-15 in 100% steam. During the steam treatment, many four-coordinated Al species are changed into six-coordinated ones, which gives rise to a large decrease of their acidity.

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieves with High Stability in High-Temperature Steam

Synthesis and characterization of ordered mesoporous aluminosilicates molecular sieves with highly hydrothermal stability

Improvement of Hydrothermal Stability of an Ordered Mesoporous Molecular Sieve Via Multistage Recrystallization

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Characterization and Investigation on the Difference of Hydrothermal Stability for Ordered Mesoporous Aluminosilicate Sieves

Synthesis of Highly Ordered and Hydrothermally Stable Mesoporous Materials Using Sodium Silicate As a Precursor

Highly steam-stable mesoporous silica assembled from preformed zeolite precursors at high temperatures

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

High temperature synthesis of hydrothermally stable micro-mesoporous silica and Al-doped mesoporous silica via rigid template

Synthesis and Characterization of the ZSM-5/MCM-41 Composite Molecular Sieves

Synthesis and characterization of a new mesoporous molecular sieve

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Highly hydrothermal stability of ordered mesoporous aluminosilicates Al-SBA-15 with high Si/Al ratio

Synthesis of ultrastable ordered mesoporous aluminosilicates molecular sieves with “hard template”

A novel mesoporous silica-clay composite and its thermal and hydrothermal stabilities

Synthesis and Characterization of Al-Msu-S Mesoporous and Meso-Microporous Molecular Sieves and Their Catalytic Performance

Synthesis of Mesoporous Materials with High Hydrothermal Stability from Mcm-22

The Synthesis and Hydrothermal Stability Test of Mesoporous Molecular Sieve with Micropores