Abstract:Mesoporous silicates synthesized in strongly basic media from sodium silicate in the presence of cetyltrimethylammonium chloride, a cationic surfactant. The formation of a lamellar phase and its transformation into hexagonal MCM-41 were studied by powder X-ray diffraction (XRD), Si-29 magic-angle-spinning (MAS) NMR and transmission electron microscopy (TEM). The gel mixture (pH > 14) is transparent. Upon acidification, a layered phase with interplanar spacing d = 35 Angstrom rapidly forms at pH = 13 and gradually transforms into the lamellar phase with d = 31 Angstrom. The Si-29 MAS NMR spectrum of the layered phase is broad and dominated by the resonance from Si(OSi)(3)O-M+ (Q(3)) structural units (M stands for the surfactant cation). The spectrum of the lamellar phase is well resolved with a more intense line from the Si(OSi)(4) (Q(4)) structural units, indicating a more regular atomic arrangement. The hexagonal phase is obtained at pH = 11.5 upon acidification of the gel, or when the pH of the intermediate product containing the lamellar phase is adjusted to 7-9 and the hydrothermal treatment continued. The hexagonal phase gives a broad Si-29 NMR spectrum dominated by the Q(4) resonance, indicating a less ordered local atomic arrangement in comparison with the lamellar phase. We suggest that the transformation is driven by the increasing reactivity of the silicate species with increasing acidity of the gel, which facilitates further aggregation of uncondensed silicate between the layers.

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

Synthesis of Mesoporous Materials with Secondary Building Units of Zeolite using Mixed Cationic-Nonionic Surfactants as Templates

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

The Synthesis of Mesoporous Molecular Sieve MCM-48

The Synthesis Of Mesoporous Molecular Sieves

Enhanced acidity and hydrothermal stability of mesoporous aluminosilicate with secondary building units characteristic of zeolite Beta

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

Study on the hydrothermal stability of MCM-41 via secondary restructure

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieve from Natural Halloysite

High-Surface-Area Zeolitic Silica with Mesoporosity

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieves with High Stability in High-Temperature Steam

Synthesis and Characterization of Mesoporous Zirconia Molecular Sieve

Synthesis and characterization of a new mesoporous molecular sieve

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Transformation of Lamellar Silicate into the Mesoporous Molecular Sieve MCM-41

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Synthesis of ultrastable ordered mesoporous aluminosilicates molecular sieves with “hard template”

Synthesis of Stable Mesoporous Molecular Sieve from Kaolin