Abstract:Mesoporous Y composites which exhibit both crystallized micropores and large mesopores with narrow mesopore diameter distributions and controlled pore diameters were successfully synthesized. The composite is synthesized through an elaborate design of the SiO2@cationic surfactant cetyltrimethylammonium bromide (SiO2@CTAB) micelle swelled by an appropriate amount of 1,3,5-trimenthylbenzene (TMB); it is subsequently fabricated from the condensing of the Y zeolite precursors, which contain Y zeolite seeds, on the mesoscale micelle followed by a hydrothermal crystallization process. The effect of synthesis conditions such as the amounts of CTAB, TMB and TEOS added to the synthesis system on the physicochemical properties of the obtained products was examined. The as-synthesized materials were carefully characterized by employing XRD, N-2 adsorption-desorption, SEM, TEM and pyridine-adsorbed FTIR techniques. The mesoporous Y zeolite exhibited both the typical diffraction characteristics of Y zeolites in the wide-angle XRD pattern, and the typical diffraction characteristics of a narrowly dispersed mesopore structure in the small-angle XRD pattern is successfully synthesized for the first time. Finally, the adsorption capacity for DBT and 4,6-DMDBT by samples with different mesopore diameters were assessed by a batch method. Sample MY-0.5C-0.35T-0.9B showed the highest capacity for adsorbing DBT in model diesel, and sample MY-0.5C-0.35T-1.5B showed the highest capacity for adsorbing 4,6-DMDBT in model diesel. Most importantly, sample MY-0.5C-0.35T-1.5B showed the highest adsorptive rate for both DBT and 4,6-DMDBT, which is at least 10 times faster than that of sample MY-0C-0.35T-0B because of the elimination of the diffusion limitation.

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Synthesis of Mesoporous Materials with Secondary Building Units of Zeolite using Mixed Cationic-Nonionic Surfactants as Templates

Continuous Synthesis of Mesoporous Y Zeolites from Normal Inorganic Aluminosilicates and Their High Adsorption Capacity for Dibenzothiophene (DBT) and 4,6-Dimethyldibenzothiophene (4,6-DMDBT)

Preparation of Mesoporous Molecular Sieves Al-Msu-S Using Ionic Liquids As Template

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

The Synthesis Of Mesoporous Molecular Sieves

Synthesis, characterization and influence parameters on the overgrowth of micro/mesoporous Y-zeolite-MCM-41 composite material under acidic conditions

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Synthesis of ultrastable ordered mesoporous aluminosilicates molecular sieves with “hard template”

Mesoporous Y zeolite through ionic liquid based surfactant templating

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieves with High Stability in High-Temperature Steam

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieve from Natural Halloysite

Generalized Synthesis of Core–shell Structured Nano-Zeolite@ordered Mesoporous Silica Composites

The Synthesis of Mesoporous Molecular Sieve MCM-48

Synthesis and characterization of ordered mesoporous aluminosilicates molecular sieves with highly hydrothermal stability

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

New Strategy To Synthesis Of Hierarchical Mesoporous Zeolites

Synthesis and Characterization of Mesoporous Zirconia Molecular Sieve

Transformation of Lamellar Silicate into the Mesoporous Molecular Sieve MCM-41