Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Zhendong Zhang,Xiaoxia Yan,Bozhi Tian,Chengzhong Yu,Bo Tu,Guangshan Zhu,Shilun Qiu,Dongyuan Zhao

DOI: https://doi.org/10.1016/j.micromeso.2005.10.026

IF: 5.876

2006-01-01

Microporous and Mesoporous Materials

Abstract:Ordered mesoporous silicates with tailorable pore structures and small pore sizes have been synthesized by using polyoxyethylene alkyl amine surfactant PN-430 [CH3(CH2)17N(EO)x(EO)y, x+y=5] as a structure-directing agent under acidic condition. Two-dimensional (2-D) hexagonal (p6mm) mesoporous silicates have been prepared via an evaporation-induced self-assembly (EISA) process. The N2 sorption isotherms show that the product has a small uniform pore size distribution of 1.8nm by BJH model, a BET surface area of 730m2/g and a pore volume of 0.36cm3/g. 3-D cubic (Pm-3n) mesoporous silicate with small uniform pore size (∼1.76nm) can also be prepared at high concentration of PN-430 by EISA method in tetrahydrofuran solvent. The solvothermal post-treatment by n-hexane at 70°C for 3d to the above material results in the phase transition of the mesostructure from Pm-3n to P63/mmc based on XRD and TEM analyses. In comparison, by using nonionic oligometric alkyl-ethylene oxide surfactant such as Brij 78 (C18H37EO20) or Triton X-100 (CH3C(CH3)2CH2C(CH3)2C6H4 EO10) as co-templates, high-quality hexagonal (p6mm) small pore mesoporous silicates have also been prepared in ethanol media. Our results show that the blend templates composed of PN-430 and a small amount of nonionic surfactant can increase the efficiency of organic and inorganic hybrid species assembly, improve the quality of the structural regularity, and decrease the pore size to about 1.65nm.