Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

A Facile Preparation of Transparent and Monolithic Mesoporous Silica Materials

High-Surface-Area Zeolitic Silica with Mesoporosity

A novel bulk sol-gel process to prepare monolithic silica materials

Synthesis of Mesoporous Silica Materials via Nonsurfactant Urea-Templated Sol-Gel Reactions

Hierarchically macro/mesoporous silica monoliths constructed with interconnecting micrometer-sized unit rods

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework

Surfactant-Template Synthesis of Mesoporous Silica Monolith Via Fast Sol-Gel Process

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Facile Synthesis of Transparent Mesostructured Composites and Corresponding Crack-Free Mesoporous Carbon/Silica Monoliths

Fabrication of the Monolithic Materials Via Novel Monocomponent Sol-Gel Process

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

A Fast Way for Preparing Crack-Free Mesostructured Silica Monolith

Mesoporous silica obtained with methyltriethoxysilane as co-precursor in alkaline medium

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Preparation Of Porous Aminopropylsilsesquioxane By A Nonhydrolytic Sol-Gel Method In Ionic Liquid Solvent

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Ultrasonic preparation of mesoporous silica using pyridinium ionic liquid

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores