Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

A novel bulk sol-gel process to prepare monolithic silica materials

Fabrication of the Monolithic Materials Via Novel Monocomponent Sol-Gel Process

A Facile Preparation of Transparent and Monolithic Mesoporous Silica Materials

Surfactant-Template Synthesis of Mesoporous Silica Monolith Via Fast Sol-Gel Process

A Fast Way for Preparing Crack-Free Mesostructured Silica Monolith

Preparing silica aerogel monoliths via a rapid supercritical extraction method

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Synthesis of crack-free silica monoliths with cubic mesostructures by a fast evaporation process

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

High-Surface-Area Zeolitic Silica with Mesoporosity

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Preparation of Monolithic Borophosphosilicate Glass by the Sol-Gel Method

Synthesis of Mesoporous Silica Using the Sol-Gel Approach: Adjusting Architecture and Composition for Novel Applications

Synthesis of porous silica gel and study on the adsorption of cerium

Application of Silica Sol-Gel in Colloidal Forming of Ceramics

A Novel Preparation Process for Thermally Stable Ultrafine Tetragonal Zirconia Aerogel

Synthesis and Characterization of Three-Dimensionally Ordered Macroporous Silica

Novel 0D-nanocarbon-silica ceramic composites: sol-gel synthesis and high-temperature evolution

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework