Abstract:A family of highly ordered mesoporous (20-300 Angstrom) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic 1m (3) over bar m, cubic Pm (3) over bar m (or others), 3-d hexagonal (P6(3)/mmc), 2-d hexagonal (p6mm), and lamellar (L-alpha) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm (3) over bar m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)(10)OH (C16EO10) surfactant species, while a 3-d hexagonal (P6(3)/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesostructured silica at room temperature. Hexagonal mesoporous silica structures with d(100) spacings of 64-77 Angstrom can be synthesized at 100 degrees C by using oligomeric nonionic surfactants. Highly ordered hexagonal mesoporous silica structures (SBA-15) with unusually large d(100) spacings of 104-320 A have been synthesized in the presence of triblock poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) copolymers. SBA-15 mesoporous structures have been prepared with BET surface areas of 690-1040 m(2)/g, pore sizes of 46-300 Angstrom, silica wall thicknesses of 31-64 Angstrom, and pore volumes as large as 2.5 cm(3)/g. A novel cubic (Im (3) over bar m) cage-structured mesoporous silica structure (SBA-16) with a large cell parameter (a = 176 ii) has been synthesized using triblock copolymers with large PEO segments. The EO/PO ratio of the copolymers can be used to control the formation of the silica mesophase: lowering this ratio of the triblock copolymer moieties promotes the formation of lamellar mesostructured silica, while higher ratios favor cubic mesostructured silica. Cubic mesoporous structures are also obtained when star diblock copolymers are used as structure-directing agents. The calcined ordered mesoporous silicas reported in this paper an thermally stable in boiling water for at least 48 h. The assembly of the inorganic and organic periodic composite materials appears to lake place by a hydrogen bonding (S-0 H+)(X-I+) pathway. The assembly race r increases with increasing concentration of [H+] and [Cl-], according to the kinetic expression r = k[H+](0.31)[Cl-](0.31).

Hierarchically macro/mesoporous silica monoliths constructed with interconnecting micrometer-sized unit rods

In-situ construction of hierarchically porous MOF monoliths using high internal phase emulsion templates

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Mesoporous silicas of hierarchical structure by hydrothermal surfactant-templating under mild alkali conditions

Controlling the primary particle evolution process towards silica monoliths with tunable hierarchical structure.

Synthesis and Characterization of Hierarchically Ordered Porous Silica Materials

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Construction and Preparation Mechanism of Hierarchically Porous Sio2 Monoliths

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Facile synthesis of hierarchically mesoporous silica particles with controllable cavity in their surfaces.

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Hierarchically Porous Silica with Ordered Mesostructure from Confinement Self-Assembly in Skeleton Scaffolds

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Functional silica monoliths with hierarchical uniform porosity as continuous flow catalytic reactors

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Synthesis and Characterization of Three-Dimensionally Ordered Macroporous Silica