Synthesis and Characterization of Hierarchically Ordered Porous Silica Materials

T. Sen,G. J. T. Tiddy,J. L. Casci,M. W. Anderson

DOI: https://doi.org/10.1021/cm034946u

IF: 10.508

2004-05-06

Chemistry of Materials

Abstract:A series of hierarchically ordered porous silica composites were synthesized using anionic (SO4 -2) polystyrene spheres and triblock copolymers Pluronic F127 (EO107PO70EO107) and P123 (EO20PO70EO20) as templates in the presence of cosurfactants (n-alcohols) in an acidic medium. The silica materials were characterized by XRD, SEM, TEM, Hg porosimetry, N2 adsorption, solid-state NMR, and TG-DTA. At least three distinct pore sizes are observed in these materials. The composites consist of three-dimensional ordered macrospheres (200−800 nm) with interconnecting uniform-sized (70−130 nm) windows. The walls of these macrospheres consist of mesostructured pores (3−8 nm). Nitrogen adsorption indicates the presence of microporosity (<2 nm). Here, we report the detailed synthesis and characterization of such hierarchically ordered porous silica composites (Sen et al. U.K. Patent, GB 0201951.1; Angew. Chem., Int. Ed. 2003, 42, 4649) with macro−meso−microporous structure and a three-dimensional interconnectivity. These materials could be useful as potential supports for heterogeneous catalysis for bulkier molecules where diffusion of reactant molecules could be facilitated.

materials science, multidisciplinary,chemistry, physical