Abstract:Hierarchical meso-macroporous materials have attracted much attention due to their potential applications in catalysis, sorption, and separation. The incorporation of interconnected macropores in mesoporous materials is very useful because macropores can favor mass transfer and reduce transport limitations. However, it still remains a challenge to fabricate ordered mesoporous channels in the bicontinuous macroporous framework walls. This paper reports a double-templating route based on a sol-gel method to prepare hierarchical meso-macroporous silica monoliths. The obtained material shows a bicontinuous macroporous structure with highly ordered meso-channels distributing inside the macroporous skeleton walls. The bimodal pore structure was formed Under the action of the two templates. The organic polymer was added to induce a phase separation taking place at the sol-gel transition and thus form the bicontinuous macroporous structure. Meanwhile, a nonionic surfactant was introduced to template the formation of ordered mesostructure inside the macroporous skeleton walls. As characterization by scanning electron microscopy, transmittance electron microscopy, N-2,, physisorption, and X-ray diffraction, the resulting silica monolith exhibits Specific Surface area as high as 880 m(2)/g and pore volume as large as 1.2 cm(3)/g. The hexagonally ordered mesopores are highly centered at 5.8 nm. Besides, through optimizing the synthesis procedure, the monolith morphology of the resulting materials can be perfectly preserved during the wet gel drying process, and thus a crack-free hierarchical silica monolith with centimeter scale can be obtained.

Template Synthesis of 3-D Bimodal Ordered Porous Silica

Synthesis of 3-D Ordered Macroporous Silicate Using the Template Formed from Monodispersed Polystyrene Latex

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Synthesis and Characterization of Three-Dimensionally Ordered Macroporous Silica

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Synthesis of 3D Ordered Porous Polystyrene Using Silica Template

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Ordered bimodal mesoporous silica with tunable pore structure and morphology

Template Effects of the Ordered Film Formed from Monodispersed Polystyrene Latex

Synthesis of Silicate Materials with Micro/Macroporous Bimodal Pore Systems

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

Synthesis of mesoporous silica using block copolymer-cationic surfactant mixtures as templates

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Preparation and characterization of bimodal mesoporous montmorillonite by using single template

Electron Microscopy and Nitrogen Adsorption Studies of Film-Type Carbon Replicas with Large Pore Volume Synthesized by Using Colloidal Silica and Sba-15 As Templates

A novel tailored bimodal porous silica with well-defined inverse opal microstructure and super-microporous lamellar nanostructureElectronic supplementary information (ESI) available: Fig. S1. See http://www.rsc.org/suppdata/cc/b3/b307444g/

Synthesis of Ordered Three-Dimensional Large-pore Mesoporous Silica and Its Replication to Ordered Nanoporous Carbon

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis and Characterization of Hierarchically Ordered Porous Silica Materials