Abstract:Highly ordered hexagonal mesoporous silica materials (JLU-20) with uniform pore sizes have been successfully synthesized at high temperature (150-220degreesC) by using fluorocarbon-hydrocarbon surfactant mixtures. The fluorocarbon-hydrocarbon surfactant mixtures combine the advantages of both stable fluorocarbon surfactants and ordered hydrocarbon surfactants, giving ordered and stable mixed micelles at high temperature (150-220degreesC). Mesoporous JLU-20 shows extraordinary stability towards hydrothermal treatment (100% steam at 800degreesC for 2 h or boiling water for 80 h), thermal treatment (calcination at 1000degreesC for 4 h), and toward mechanical treatment (compressed at 740 MPa). Transmission electron microscopy images of JLU-20 show well-ordered hexagonal arrays of mesopores with one-dimensional (M) channels and further confirm that JLU-20 has a two-dimensional (2D) hexagonal (P6mm) mesostructure. Si-29 HR MAS NMR spectra of as-synthesized JLU-20 shows that JLU-20 is primarily made up of fully condensed Q(4) silica units (delta = - 112 ppm) with a small contribution from incompletely cross-linked Q(3) (delta = - 102 ppm) as deduced from the very high Q(4)/Q(3) ratio of 6.5, indicating that the mesoporous walls of JLU-20 are fully condensed. Such unique structural features should be directly attributed to the high-temperature synthesis, which is responsible for the observed high thermal, hydrothermal, and mechanical stability of the mesoporous silica materials with well-ordered hexagonal symmetry. Furthermore, the concept of "high-temperature-synthesis" is successfully extended to the preparation of three-dimensional (3D) cubic mesoporous silica materials by the assistance of a fluorocarbon surfactant as a co-template. The obtained material, designated JLU-21, has a well-ordered cubic Im3m mesostructure with fully condensed pore walls and shows unusually high hydrothermal stability, as compared with conventional cubic mesoporous silica materials such as SBA-16.

Ultralow Temperature Synthesis of Ordered Hexagonal Smaller Supermicroporous Silica Using Semifluorinated Surfactants As Template.

Semi-fluorinated Surfactant Syntheses of Ordered Porous Materials with Tailorable Pore Sizes

High-temperature synthesis of stable ordered mesoporous silica materials by using fluorocarbon-hydrocarbon surfactant mixtures.

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Ordering improvement of mesoporous silica materials templated from semi-fluorinated nonionic surfactants by introduction of organic additives

Low-Temperature Strategy To Synthesize Highly Ordered Mesoporous Silicas With Very Large Pores

Hydrothermal Synthesis of Ordered Mesoporous Silicas with Extraordinarily Ultra-low Dielectric Constants

Highly steam-stable mesoporous silica assembled from preformed zeolite precursors at high temperatures

High‐Temperature Generalized Synthesis of Stable Ordered Mesoporous Silica‐Based Materials by Using Fluorocarbon–Hydrocarbon Surfactant Mixtures

Ordered cubic mesoporous silicas with large pore sizes synthesized via high-temperature route.

Low temperature strategy to synthesize high surface area mesoporous hydroxypropyl-β-cyclodextrin-based silicas via benign template removal

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

High-temperature Synthesis of Ordered Mesoporous Silicas from Solo Hydrocarbonsurfactants and Understanding of Their Synthetic Mechanisms

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

A Series Of Highly Ordered, Super-Microporus, Lamellar Silicas Prepared By Nanocasting With Ionic Liquids

A novel low temperature vapor phase hydrolysis method for the production of nano-structured silica materials using silicon tetrachloride

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Tailoring pore structures and morphologies of highly ordered cubic mesoporous silica prepared in mild conditions: the effects of reaction parameters

Preparation of Nano-Sized Mesoporous Silica Dioxide and Al-Doped Silica Dioxide at Extremely Low Reactant Concentration