Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Large size and low density SiOC aerogel monolith prepared from triethoxyvinylsilane/tetraethoxysilane

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Sol-gel synthesis of preceramic polyphenylsilsesquioxane aerogels and their application toward monolithic porous SiOC ceramics

Preparation and Structural Evolution of SiOC Preceramic Aerogel During High-Temperature Treatment

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Preparation and High Temperature Inorganic Transformation of Flexible Silicone Aerogels

Monolithic carbon aerogels within foam framework for high-temperature thermal insulation and organics absorption

Preparation and Characterization of Composite SiO2 Aerogel by a Novel One-step Modified Process

Preparation and structural characterization of SiO2-ZrO 2 aerogels

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Preparation and Characterization of Silica-Titania Aerogel Monoliths by Sol-Gel Method

Heat-resistant, strong alumina-modified silica aerogel fabricated by impregnating silicon oxycarbide aerogel with boehmite sol

Preparation of the methyltriethoxysilane based aerogel monolith with an ultra-low density and excellent mechanical properties by ambient pressure drying

New BN/SiOC aerogel composites fabricated by the sol-gel method with excellent thermal insulation performance at high temperature

Preparation and Structural Characterization of SiO2-ZrO2 Aerogels

High Compression Strength and Thermal Insulation Silica Aerogel Monolith with Scaffold of a Cyclic Olefin Siloxane Co-Oligomer Via Ambient Pressure Drying

Effect of Gelation Initiators on Microstructure and Thermal Stability of Y2O3-SiO2 Composite Aerogels

Preparation of monolithic titania aerogels with high surface area by a sol–gel process combined surface modification

Preparation of monolithic Al2O3–SiO2 aerogels with high-temperature resistance using boehmite nanorods

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum