Abstract:Silica aerogel is a unique nanomaterial with three-dimensional nano-porous networks. However, the microstructures of aerogels are easily damaged at high temperatures environment, weakening the thermal insulation performance. In this work, we prepared thermally stable SiOC nanospheres and then composited them with aerogel matrix. SiOC nanospheres and aerogel matrix have excellent compatibility. SiOC nanospheres can induce the aerogel matrix forming island microstructures after drying process. The presence of the island microstructure leads to a reduce of the inter-skeleton macropore size, which declines from 4.77 μm to 2 μm. The thermal conductivity decreases from 0.0813 to 0.0646 W/ (m K). The volume shrinkage and density also show a clear downward trend. In order to investigate the impact of high-temperature to thermal insulation performance, the aerogel composites are experienced different high-temperature treatment. The results demonstrate that the island microstructure of aerogel is transformed into a spherical shape after high-temperature treatment. The particle diameter increases from 5 μm to 5.7 μm when treated in 200 °C and 400 °C. Upon 400 °C, the diameter reduces from 5.7 μm to 4.4 μm at 800 °C. The variety in the size of the aerogel skeleton particles results in a reduction in the pore diameters of the interskeleton pores from 8 to 3.8 μm. The thermal conductivity decreases from 0.0667 to 0.0466 W/ (m K) treating below 400 °C and increases to 0.0712 W/ (m K), when heat treatment temperature is 800 °C. The enhancement of thermal insulation performance is attributed to the decline of macropores content between skeletons caused by swelling of aerogel particles. The diameters of macropores between skeletons reduce, which can effectively weaken the influence of gaseous heat transfer. This work provides a reference for the preparation of aerogel composites that can maintain excellent thermal insulation properties in high-temperature environment.

New BN/SiOC aerogel composites fabricated by the sol-gel method with excellent thermal insulation performance at high temperature

SiOC nanospheres reinforced silica aerogel with excellent compatibility and excellent thermal insulation under high temperature conditions

Konjac glucomannan-based aerogels with excellent thermal stability and flame retardancy for thermal insulation application

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

Fabrication of the SiC/HfC Composite Aerogel with Ultra-Low Thermal Conductivity and Excellent Compressive Strength

High-temperature microtexture, microstructure evolution, and thermal insulation properties of porous Si3N4/silica aerogel composites produced by impregnation

Thermal stable, fire-resistant and high strength SiBNO fiber/SiO2 aerogel composites with excellent thermal insulation and wave-transparent performances

Preparation of the Novel B4C–SiC Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Lightweight, Strong, and Super-Thermal Insulating Polyimide Composite Aerogels under High Temperature

Preparation and Properties of Highly Transparent SiO2 Aerogels for Thermal Insulation

SiO2 aerogel multiscale reinforced by glass fibers and SiC nanowhiskers for thermal insulation

Fabrication of Al2O3 aerogel-SiO2 fiber composite with enhanced thermal insulation and high heat resistance

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Novel silica-modified boehmite aerogels and fiber-reinforced insulation composites with ultra-high thermal stability and low thermal conductivity

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Ultralight and compressive SiC nanowires aerogel for high-temperature thermal insulation

Anisotropic and high-strength SiO2/cellulose nanofiber composite aerogel with thermal superinsulation and superhydrophobicity

Robust, lightweight gelatin composite aerogel with outstanding thermal insulation

Anisotropic thermally superinsulating boron nitride composite aerogel for building thermal management

Flexible SiC nanowire aerogel with excellent thermal insulation properties