Abstract:The study results of introduction of barium-strontium carbonatite of various fractional composition into flux based on silicomanganese production slag are presented. The principal possibility of using their mixtures for depositing and welding of low-alloy steels is shown, while the use of barium-strontium carbonatite makes it possible to reduce contamination of weld metal with nonmetallic inclusions. In series of experiments in laboratory conditions, various compositions of welding fluxes were made and investigated. As components, barium-strontium modifier BSC produced by “NPK Metallotechnoprom” LC under TU 1717-001-75073896-2005 was used, wt. %: 13.0 – 19.0 % BaO; 3,5 – 7,5 % SrO; 17.5 – 25.5 % CaO; 19.8 – 29.8 % SiO2 ; 0.7 – 1.1 % MgO; 2.5 – 3.5 % K2O; 1.0 – 2.0 % Na2O; 1.5 – 6.5 % Fe2O3 ; 0 to 0.4 % MnO; 1.9 – 3.9 % of Al2O3 ; 0.7 – 1.1 % TiO2 ; 16.0 – 20.0 % CO2 as well as silicomanganese slag produced by JSC “EVRAZ – West-Siberian Metallurgical Combine”, wt. %: 6.91 – 9.62 % Al2O3 ; 22.85 – 31.70 % CaO; 46.46 – 48.16 % SiO2 ; 0.27 – 0.81 % FeO; 6.48 – 7.92 % MgO; 8.01 – 8.43 % MnO; 0.28 – 0.76 % F; 0.26 – 0.36 % Na2O; up to 0,62 % K2O; 0.15 – 0.17 % S; 0.01 % P. Basis of the flux is silicomanganese production slag, into which a flux additive was introduced. Flux additive was produced in two ways. The first one: by mixing barium-strontium modifier with liquid glass in a ratio of 75 and 35 %, respectively. The second variant is as follows: dust of strontium-barium modifier of fraction less than 0.2 mm was used as a flux additive. The technology of flux-additive manufacturing is described. Welding of rollers was carried out using ASAW-1250 welding tractor. Regimes of surfacing were worked out. The chemical compositions of fluxes, slag crusts, flux and weld metal were determined. Metallographic studies of metal were performed. The results of analysis for presence of nonmetallic inclusions in weld zone were carried out in accordance with GOST 1778 – 70. Studies indicate a decrease in contamination of weld metal by silicates that are not deformed and absence of brittle silicates.

THE CLASSIFICATION OF SILICOCALCIUM-BARIUM ALLOYS AND THEIR APPLICATION TO STEEL LADLE PROCESSING

PHASE FORMATION DURING STEEL REFINING BY ALLOYS WITH ALKALINE EARTH ELEMENTS (Ba, Mg, Sr)

THE ANALYSIS OF STRUCTURE-CHEMICAL STATE OF DUPLEX SYSTEM OF SILICATES-SILICIDES OF ALKALINE EARTH METALS

Synergistic Effect of Calcium and Barium on Non-metallic Inclusions Modification and Improvement in Steel Cleanliness

Phase equilibrium in aluminum and calcium treatment economically alloyed manganese steel in units lined with magnesite-based refractories

Research of Si-Ca-Ba Compound Deoxidizer Composition Optimization for Steelmaking

Thermodynamic features of the modifi cation of non-metallic inclusions by calcium in low-carbon steels deoxidized by aluminum

APPLICATION OF BARIUM-STRONTIUM CARBONATITE FOR PRODUCTION OF WELDING FLUXES BASED ON SILICOMANGANAZE PRODUCTION SLAG

Effect of Refining Slag Composition on Inclusions in Molten Steel treated by Barium‐bearing Alloy

A qualitative and quantitative investigation of nonmetallic inclusions in molten Al–Mg, Al–Cu, and Al–Zn–Mg–Cu alloys

Combined Treatment of Sr and B and Evaluation of Refinment-Modification Levels for Al-7si Casting Alloy

Effect of Deoxidizing and Alloying Routes on the Evolution of Non-Metallic Inclusions in 55SiCr Spring Steel

Thermodynamic examination of inclusion modification and precipitation from calcium treatment to solidified steel

Experimental determination of the phase equilibria of aluminum-rich Al−Li−Cu alloys

Phase equilibrium occurring during low-carbon iron-based melt deoxidation with silicostrontium

Effect of FeSi Alloy Additions and Calcium Treatment on Non-Metallic Inclusions in 304 Stainless Steel during AOD and LF Refining Process

Effect of rare earth La–Ce on solidification structure of 3.2%Si-0.9%Al non-oriented silicon steel

Thermodynamic analysis of processes in the high-temperature polycomponent Fe–Y–Si–O–C system

Influence of refining slag composition on nonmetallic inclusions in 38CrMoAl steel

Quantitative and Qualitative Evaluation of Non-Metallic Inclusions in High-Silicon Steel after Hot Rolling

The effect of complex extra-furnace treatment of metal melts on the formation of non-metallic inclusions in large-sized ingots