Abstract:In this paper, the effect of BaCu(B 2 O 5 ) addition on the sintering process, phase composition, microstructure and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics were investigated by the conventional solid-state reaction technique. It was suggested that the liquid phase of BaCu(B 2 O 5 ) was responsible for the densification of the BaO–0.6ZnO–2.9TiO 2 ceramics at approximate 900 °C. Using EDX analysis the evaporating of boron was confirmed and Cu 2+ most likely substituted for Zn 2+ sites in the phases Ba 4 ZnTi 11 O 27 and BaZn 2 Ti 4 O 10 . BaTiO 3 phase appearing at the grain boundary as the derivative of BaCu(B 2 O 5 ) had a considerable negative effect on the microwave dielectric properties. The variation tendency of dielectric constant was increased in accord with the trend between bulk densities and the sintering temperature. The maximum Q × f value of 15200 GHz was obtained for the specimen with 7 wt% BaCu(B 2 O 5 )The specimen with 7 wt% BaCu(B 2 O 5 ) addition sintered at 900 °C for 1.5 h showed dense microstructure and had acceptable microwave dielectric properties: dielectric constant ε r = 37, Q × f = 15200 GHz and the temperature coefficient of resonant frequency τ f = −9.8 ppm/°C.

Low Temperature Sintering Kinetics of BaO-0.15ZnO-4TiO2 Dielectric Ceramic in the Presence of a Liquid Phase

Low Temperature Sintering Kinetics of Bazn2ti4o11 Dielectric Ceramic in the Presence of A Liquid Phase

A Synergistic Effect of Li-B-Si Glass and La-B on Low-Temperature Sintering of Bao-0.15zno-4tio(2) Dielectric Ceramic

Low Temperature Sintering Kinetics and Microwave Dielectric Properties of BaTi5O11 Ceramic

Investigation of Low-Temperature Sintering Mechanism on BaONd2O3TiO2 Dielectric Ceramics with Li2OB2O3-SiO2 and BaOZnOB2O3 Glasses

Influence of Li2O–B2O3–SiO2 Glass on the Sintering Behavior and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO2 Ceramics

Effects of Li2O-B2O3-SiO2 glass on the low-temperature sintering of Zn0.15Nb0.3Ti0.55O2 ceramics

Low-temperature Sintering and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO 2 Ceramics with Li 2 O–B 2 O 3 –sio 2 Addition

Low Temperature Sintering of BaO–ZnO–TiO2 Ceramics for LTCC Applications

Low Temperature Sintering of Zn1.8sio3.8 Dielectric Ceramics Containing 3Zno-2B(2)o(3) Glass

Low-temperature sintering of (Zn0.8 Mg0.2)2SiO4–TiO2 ceramics

Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Low Temperature Sintering and Dielectric Properties of BaTi_(0.75)Zr_(0.25)O_3 Ceramic

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Low-temperature firing and microwave dielectric properties of Ba–Nd–Ti with composite doping Li–B–Si and Ba–Zn–B glasses

Low-temperature sintering kinetics and dielectric properties of Ba5Nb4O15 with B2O3–SiO2 glass

Low Temperature Sintering Of Low-Loss Zntio3 Microwave Dielectric Ceramics With Zn-B-Si Glass

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

Low‐temperature co‐fired ceramic application of SmTaO4 and YTaO4 with ZnO‐B2O3‐SiO2 additive