Abstract:The effect of different heat inputs of 1.45 kJ/mm, 1.78 kJ/mm and 2.31 kJ/mm on the microstructure and mechanical properties of deposited metals of the self-developed AWS A5.28 E120C-K4 high strength steel flux-cored wire was studied by optical microscope, scanning electron microscope and mechanical property test. With the increase in heat input, the results showed that the microstructure of deposited metals became coarse. Acicular ferrite increased at first and then decreased, granular bainite increased and degenerated upper bainite and martensite decreased slightly. Under the low heat input of 1.45 kJ/mm, the cooling rate was fast and the element diffusion was uneven, which caused composition segregation and easy to form large size inclusions SiO2-TiC-CeAlO3 with weak binding to the matrix. Under the middle heat input of 1.78 kJ/mm, the composite rare earth inclusions in dimples were mainly TiC-CeAlO3. The dimples were small and uniformly distributed, and the dimple fracture mainly depended on the wall-breaking connection between medium-sized dimples rather than an intermediate media. Under the high heat input of 2.31 kJ/mm, SiO2 was easy to adhere to high melting point Al2O3 oxides to form irregular composite inclusions. Such irregular inclusions do not need to absorb too much energy to form necking. Finally, the integrated effects of microstructure and inclusions resulted in the optimum mechanical properties of deposited metals with a heat input of 1.78 kJ/mm, which was a tensile strength of 793 MPa and an average impact toughness at -40 °C of 56 J.

Effect of Inoculation with Cored Wire Injection on Microstructure Features of Axial Large-size High Chromium Cast Iron

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effects of Inoculation on the Pearlitic Gray Cast Iron with High Thermal Conductivity and Tensile Strength

Influence of Inoculation on the Mass Effect in Heavy Section Ferritic Spheroidal Graphite Cast Iron

The Influence of Ni Content on the Microstructure and Impact Wear Resistance Performance of High-Chromium Casting Infiltration Coating

Investigation of microstructure evolution and mechanical properties of near-eutectic Fe2-CoNiCr C high entropy cast iron

Effect of (nbti)c Particles on the Microstructure and Hardness of High Chromium and Nickel Indefinite Chilled Cast Iron

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

The Effects of MgFeSi and Inoculant Selection on Microstructure and Mechanical Properties of Varying Section Size Ductile Iron Castings

Effect of Chromium on Microstructure and Properties of High Boron White Cast Iron

Interface characteristics and mechanical properties of wire-arc depositing Inconel 625 superalloy on ductile cast iron

Effect of Multi-Element Microalloying on the Structure and Properties of High Chromium Cast Iron

Effect of cobalt content on the microstructure, microtexture, and mechanical properties of W-Ni-Fe-xCo alloys during solid-phase-sintering and liquid-phase-sintering

Effect of Carbon on the Microstructure Evolution and Mechanical Properties of Low Si-Containing Centrifugal Casting 20cr32ni1nb Alloy

Effect of Sb–Ba–Ce–Si–Fe Post Inoculants on Microstructural and Mechanical Properties of As‐Cast Pearlitic Ductile Iron

Effect of Heat Input on Microstructure and Mechanical Properties of Deposited Metal of E120C-K4 High Strength Steel Flux-Cored Wire

L1 2 strengthening of WC-CoNiFe cemented carbides by spark plasma sintering

Development of a Ni–Cr–Mo–V Alloyed Ductile Iron with High Hardness

Improvement in microstructure and wear-resistance of high chromium cast iron/medium carbon steel bimetal with high vanadium