Abstract:Air-cooling from an intercritical (IC) temperature produced an acicular pearlite in ferrite structure and was effective in increasing the strength and ductility of ductile iron in sections up to 10 inches (250 mm). Five alloys were melted and poured as 3-inch Y-blocks, and IC heat treatment produced a fine-grained acicular pearlite + ferrite structure in all five alloys. The compositions ranged from 3.39–3.59% C, 2.34–2.45% Si, 0.29–0.44% Mn, 0.59–0.61% Cu and 0.24–1.78 % Ni, with CE ranging from 4.34 to 4.40. Samples were removed from the bottoms of the Y-blocks to obtain test samples for tensile and Charpy V-Notch (CVN) impact testing. The test samples were heat-treated at intercritical temperatures near the upper critical temperature (UCT) and cooled at various rates to simulate air-cooling of castings up to 10 inches (250 mm). Prior to intercritical heat treatment, experiments were conducted to determine the optimum heat treatment parameters. It was found that the path of the thermal cycle on heating to the IC temperature can affect the quality of the heat-treated structure. Among the things learned are the following: The lamellar austenite in ferrite structure persisted at temperatures as high as 60° F above the predicted UCT. Heat treatment at UCT + 20 °F produced the most dense, acicular pearlite + ferrite structure. Ferritizing prior to IC heat treatment minimizes the pearlite network in the cell boundaries. A minimum soak time of 2 h at the IC temperature is recommended. The lamellar structure is stable for at least 8 h. Copper appears to delay the time to reach equilibrium at the UCT. Nickel (at 1.8%) counteracts the Cu effect. The IC heat-treated samples displayed significantly higher ferrite contents over the as-cast materials. The high strength and elongation were attributed to grain refinement and increased ferrite contents, respectively. Furthermore, the material appears to be forgiving of marginal graphite structures. Despite the coarse graphite inclusions with poor shapes, 7–9% elongation was attained in test bars exceeding 60 ksi (414 MPa) yield strength when cooled as a 10-inch (250 mm) section.

The Effects of MgFeSi and Inoculant Selection on Microstructure and Mechanical Properties of Varying Section Size Ductile Iron Castings

Influence of Inoculation on the Mass Effect in Heavy Section Ferritic Spheroidal Graphite Cast Iron

Effect of Sb–Ba–Ce–Si–Fe Post Inoculants on Microstructural and Mechanical Properties of As‐Cast Pearlitic Ductile Iron

Effects of Titanium, Cerium or Aluminum Addition on Microstructure and Mechanical Properties of Ductile Iron Castings

Effects of Inoculation on the Pearlitic Gray Cast Iron with High Thermal Conductivity and Tensile Strength

The Effect of Heat Treatments on the Microstructural Evolution of Twin-Roll-Cast Al-Fe-Si Alloys

Relationships Between Macrostructure and Microstructure in Lamellar Graphite Iron Castings

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Effect of regular thicknesses on the microstructural and quantitative analysis for a hypo-eutectic ductile iron alloyed with Ni and V

Achieving Higher Strength and Ductility in Heavy-Section Ductile Iron Castings

Effect of Aluminum, Copper and Manganese on the Structure and Properties of Cast Irons

A study of cooling time, copper reduction and effects of alloying elements on the microstructure and mechanical properties of SG iron casting during machining

A scale up study on chemical segregation and the effects on tensile properties in two medium Mn steel castings

Effect of Iron-Rich Intermetallic and Eutectic Si Accumulation on Al-Si-Mg Alloy

Effect of Micro-Structural Dispersity of SiMo Ductile Iron on High Temperature Performance during Static Oxidation

The Influence Of Cast Structure On The Austempering Of Ductile Iron. Part 3. The Role Of Nodule Count On The Kinetics, Microstructure And Mechanical Properties Of Austempered Mn Alloyed Ductile Iron

The Influence of Insertion Depth of Inorganic Materials on Solidification Microstructure and Segregation of 2.5-ton 42CrMo Ingot

Microstructure and Mechanical Properties of High Boron Iron-Based Alloy Solidified in Different Moulds

Impact of carbide-promoting elements on the mechanical properties of solid-solution-strengthened ductile iron

Effect of the Fe/Mn Ratio on the Microstructural Evolution of the AA6063 Alloy with Homogenization Heat Treatment Interruption

Effect of Mn/Fe ratio on the microstructure and properties of 6061 sheets obtained by twin-roll cast