Abstract:Laser cladding (LC) has been applied to enhance the wear resistance of 316L coatings by depositing in-situ VC-Cr7C3 metal matrix composites (MMCs) coating on structural steel substrate using pre-mixed powder consisting of vanadium, carbon, and 316L stainless steel. The effects of different process parameters, varied V and C contents on the phase constituents, microstructure, and the mechanical properties of 316L LC coatings were investigated systematically. The related microstructure evolution and the mechanical properties were comprehensively studied. The results indicated that under the selected laser irradiance of 80 W/mm2, scanning rate of 4 mm/s, and powder feeding rate of 10 g/min, by increasing V and C content from 0 wt % to 14 wt %, VC, Cr7C3, and Cr23C6 would be progressively precipitated at grain boundaries, and the austenite grains tended to be refined. Consequently, the microhardness of reinforced 316L coatings significantly increased from 207 HV1 to 467.8 HV1. Wear tests showed that the wear resistance improved some 8 times compared to the pure 316L layer under the dry sliding condition, and the dominating wear mechanism for the cladding transferred from adhesive wear to abrasive wear. Further microstructure characterization revealed that besides precipitation strengthening and fine-grain strengthening, the strengthening effect was also originated from the interfacial structure between the precipitated carbides, including a coherent interface for γ/Cr7C3, semi-coherent interfaces for γ/VC, and VC/Cr7C3. Based on the results of thermodynamic calculation and Fe-Cr-C ternary phase diagram, the spherical VC acted as the nucleation sites for the dispersed carbide reinforcement and the austenite grains, and the inhibition against austenite matrix growth by ceramic precipitations dispersedly distributed along the grain boundaries.

Improvement in microstructure and wear-resistance of high chromium cast iron/medium carbon steel bimetal with high vanadium

Microstructure and abrasive wear properties of high-vanadium-chromium wear resistant alloy

Fabrication and abrasive wear property of high chromium cast iron with high vanadium and high nitrogen content (HCCI-VN)

Effect of Multi-Element Microalloying on the Structure and Properties of High Chromium Cast Iron

Microstructure and Wear Resistance of High-Chromium Cast Iron with Multicomponent Carbide Coating via Laser Cladding

The Effect of Vanadium Content Coupling with Heat Treatment Process on the Properties of Low-Vanadium Wear-Resistant Alloy

Microstructure and Wear Resistance of WC and High Chromium Cast Iron Hardfacing Layers

Friction resistance and bonding strength of high vanadium alloy steel/low carbon steel bimetal after heat treatments

Effect of Vanadium Addition on the Microstructure, Hardness, and Wear Resistance of Al 0.5 CoCrCuFeNi High-Entropy Alloy

Mechanical properties and impact abrasive wear resistance in vanadium microalloyed medium carbon CrMo cast steel strengthened with nanoprecipitates

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Investigating Microstructural Evolution and Its Influence on Tribological Behaviors of In-Situ Formed VCp Reinforced Iron-Based Composites with Variable Mn Content

Preparation and wear properties of high-vanadium alloy composite layer

Microstructure evolution and wear resistance of laser cladded 316L stainless steel reinforced with in-situ VC-Cr7C3

Preparation and wear properties of high-silicon high-vanadium wear-resistant alloy with nano pearlite matrix and carbides composite structure

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Study on microstructure and properties of laser-clad Fe-based (Ti, V)C composite coatings

Improvement of wear and hot melt loss resistance of metal carbide layers on H13 steel

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Fabrication and wear property of in-situ micro-nano dual-scale vanadium carbide ceramics strengthened wear-resistant composite layers

Enhanced strength and ductility of high chromium cast iron/low carbon steel bimetal by heterostructure design