Abstract:Extrusion-free-form printing of alumina ceramics has the advantages of low cost, short cycle time, and high customization. However, some problems exist, such as the low solid content of ceramic paste and the unsatisfactory mechanical properties of pure alumina ceramics. In this study, SiC nanoparticles were used as a reinforcement phase added to the alumina ceramic matrix. Methylcellulose is used as the binder in the raw material system. Ammonium polyacrylate is used as a dispersant to change the rheological properties of the slurry and increase the solid content of ceramics. SiC nanoparticle-strengthened alumina ceramics were successfully prepared by the extrusion process. The relative settling height and viscosity of ceramic slurries were characterized. The sintering shrinkage of composite ceramics was tested. The flexural strength, fracture toughness, and hardness of the ceramics were characterized. The strengthening and toughening mechanisms of the composite ceramics were further explained by microscopic morphology analysis. Experimental results show that when the content of the dispersant is 1 wt.%, the rheological properties of the slurry are the best. Maximum measured bending strength (227 MPa) and fracture toughness (5.35 MPa·m1/2) were reached by adding 8 wt% SiC nanoparticles; compared with pure alumina ceramics, flexural strength and fracture toughness increased by 42% and 41%, respectively. This study provides a low-cost and effective method for preparing ceramic composite parts.

Reliable High Strength Alumina Fabricated by DCC-HVCI Using Submicron Calcium Citrate Complex

Direct Coagulation Casting of Alumina Suspension from Calcium Citrate Assisted by Ph Shift

Direct coagulation casting of alumina using magnesium citrate as coagulating agent with glycerol diacetate as pH regulator

Properties of Alumina Coagulated Bodies Prepared by Direct Coagulation Casting Via High Valence Counter Ions (DCC‐HVCI)

Direct coagulation casting of alumina suspension by high valence counter ions using Ca (IO 3) 2 as coagulating agent

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

Direct coagulation casting of alumina via controlled release of calcium from ammonium polyphosphate chelate complex

Direct coagulation casting of alumina slurry and its technics

Direct coagulation casting of alumina suspension via controlled release of high valence counterions from thermo-sensitive liposomes

Direct Coagulation Casting of Positively Charged Alumina Suspension by Controlled Release of High Valence Counter Ions from Calcium Phosphate

Alumina densification at low temperatures using CaV2O6 for LTCC application

Fabrication of alumina ceramics with high flexural strength using stereolithography

Highly Reliable Yttria‐stabilized Zirconia Prepared by Direct Coagulation Casting‐high Valence Counter Ions Using Calcium Polyphosphate

Direct Coagulation Casting of Yttria-Stabilized Zirconia Using Magnesium Citrate and Glycerol Diacetate

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

The Influence of Sintering Process on the Microstructure of Submicron Alumina Fabricated by Gelcasting

Influence of mono-carbonate hydrates on mechanical properties of CAC bonded castables fired at 800 °C

Influence of High Valence Counter-ions on Rheological Properties of Alumina Suspension

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

The Effect of Boehmite on Electrokinetic Behaviours, Rheology and Coagulation for Direct Coagulation Casting of Alumina

High‐performance Al 2 O 3 ceramics prepared by DCC‐HVCI via microwave heating