Abstract:A new direct coagulation casting of aqueous alumina suspension was developed via controlled release of high valence counter ions from calcium iodate with increase in the temperature from 55 degrees C to 70 degrees C. The influence of calcium iodate on the rheology of alumina suspension was investigated. A small amount of calcium iodate increased the viscosity of the concentrated alumina suspension at high temperature and finally transformed it into a wet-coagulated body. The mechanism of coagulation is proposed such as that the solubility of calcium iodate increases with increase in temperature. The high valence Ca2+ ions diffuse into the double electrical layer of alumina particles surface through electrostatic attraction, reduces the zeta potential, hence decreases repulsive force between particles. Also reaction between Ca2+ and citrate leads to insufficient dispersant coverage on the particle surface. Both factors contribute to the coagulation of the suspension. The coagulation time was from 1 to 4 similar to h by maintaining the temperature in the range of 55 degrees C70 degrees C. The wet-coagulated bodies prepared from 50 similar to vol% alumina suspension showed a high compressive strength of 2.63.2 similar to MPa with uniform microstructure. The relative density of sintered sample is 99.4% at 1550 degrees C for 2 h with perfect microstructure.

Direct coagulation casting of alumina slurry and its technics

Direct Coagulation Casting of Alumina Suspension from Calcium Citrate Assisted by Ph Shift

Natural additives in protein coagulation casting process for improved microstructural controllability of cellular ceramics

Direct coagulation casting of alumina using magnesium citrate as coagulating agent with glycerol diacetate as pH regulator

Direct Coagulation Casting of Positively Charged Alumina Suspension by Controlled Release of High Valence Counter Ions from Calcium Phosphate

The Effect of Boehmite on Electrokinetic Behaviours, Rheology and Coagulation for Direct Coagulation Casting of Alumina

Direct coagulation casting of alumina suspension by high valence counter ions using Ca (IO 3) 2 as coagulating agent

Direct coagulation casting of alumina suspension via controlled release of high valence counterions from thermo-sensitive liposomes

Direct coagulation casting of alumina via controlled release of calcium from ammonium polyphosphate chelate complex

GELCASTING OF ALUMINA SLURRY DISPERSED IN SILICA SOL WITHOUT DE-AIRING PROCESS

Properties of Alumina Coagulated Bodies Prepared by Direct Coagulation Casting Via High Valence Counter Ions (DCC‐HVCI)

Reliable High Strength Alumina Fabricated by DCC-HVCI Using Submicron Calcium Citrate Complex

Hydrolysis-assisted Solidification of Alumina Slurry Dispersed in Silica Sol Without De-Airing Process

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

Effect of Dispersants on the Rheological Properties and Slip Casting of Concentrated Alumina Slurry

New gel-casting process for alumina ceramics based on gelation of alginate

Hydrophobic coagulation of alumina slurries

Direct Coagulation Casting of Silicon Carbide Ceramics via Dispersant Reaction

Gel-casting Without De-Airing Process Using Silica Sol As a Binder

Fabrication of Alumina Green Body Through Gelcasting Process Using Alginate

Relation Between Rheological and Curing Behavior of Inorganic Foam Slurries in the Gel-Casting Process