Abstract:This study demonstrates the successful fabrication of near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia (1.5YSZ) ceramics using current-ramp flash (CRF) sintering technique. The process involved regulating Joule heating in the samples by fine-tuning the input power through an alternating current field (nominal current density: 50 mA·mm −2 ) within a 3-minute timeframe at a furnace temperature of 1100°C. This approach effectively enhanced grain size uniformity, which is crucial for preventing sample cracking associated with spontaneous tetragonal-to-monoclinic (T→M) phase transformation, thereby promoting densification with average relative densities exceeding 99%. The highest average fracture toughness of the 1.5YSZ samples was measured at 9.2 MPa·m 0.5 using the standardized single-edge pre-cracked beam method. This toughness is approximately double that of commonly used 3YSZ samples produced by CRF sintering, all of which exhibited comparable average grain sizes and relative densities. Additionally, the 1.5YSZ samples demonstrated nearly identical resistance to low-temperature degradation (LTD) compared to the 3YSZ samples after accelerated hydrothermal aging at 140°C for 15 hours, roughly equivalent to 60 years at 37°C. The reduced yttria concentration in 1.5YSZ facilitates T→M phase transformation at lower stress thresholds, enhancing toughness through increased crack shielding from a larger volume fraction of transformed grains. Furthermore, the uniform yttria distribution in 1.5YSZ, revealed by scanning transmission electron microscopy, compensates for the reduced tetragonal phase stability and contributes to improved LTD resistance. Notably, these exceptional properties were achieved at a furnace temperature 300°C lower and with a sintering duration several hours shorter than those of conventionally-sintered counterparts.

Direct Coagulation Casting of Yttria-Stabilized Zirconia Using Magnesium Citrate and Glycerol Diacetate

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Highly Reliable Yttria‐stabilized Zirconia Prepared by Direct Coagulation Casting‐high Valence Counter Ions Using Calcium Polyphosphate

Direct coagulation casting of alumina using magnesium citrate as coagulating agent with glycerol diacetate as pH regulator

In-situ Coagulation of Yttria-Stabilized Zirconia Suspension Via Dispersant Hydrolysis Using Sodium Tripolyphosphate

Direct Coagulation Casting of Alumina Suspension from Calcium Citrate Assisted by Ph Shift

In Situ Coagulation of Yttria‐stabilized Zirconia Ceramic with Enhancement of Green Body Via Polyvinyl Pyrrolidone Crosslink

Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)

Direct Coagulation Casting of Silicon Carbide Ceramics via Dispersant Reaction

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Direct Coagulation Casting of Silicon Carbide Suspension Via Polyelectrolyte Dispersant Crosslink Reaction

Conventional sintering of nano-crystalline Yttria-Stabilized Zirconia enables high-strength, highly translucent and opalescent dental ceramics

High-strength porous YSZ ceramics fabricated by TBA-based gelcasting with high solid loading slurry

Direct Coagulation Casting of Silicon Nitride Suspension Via a Dispersant Reaction Method

Preparation of YAG Gel Coated ZrB2–SiC Composite Prepared by Gelcasting and Pressureless Sintering

Dispersion And Gelcasting Of Zirconium Diboride Through Aqueous Route

Reliable High Strength Alumina Fabricated by DCC-HVCI Using Submicron Calcium Citrate Complex

Dense and Cellular Zirconia Produced by Gel Casting with Agar: Preparation and High Temperature Characterization

Yttria-stabilized zirconia (8YSZ) synthesis in a supercritical CO 2 -assisted process: a parametric study for achieving cubic phase stability

Realizing near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia ceramics via current-ramp flash sintering