Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)

Jie Xu,Minghao Yang,Ke Gan,Yanan Qu,Xiaoyan Zhang,Ning Ma,Yali Wang,Jinlong Yang

DOI: https://doi.org/10.1016/j.ceramint.2015.11.017

IF: 5.532

2016-01-01

Ceramics International

Abstract:Lead zirconate titanate (PZT) ceramics were prepared by direct coagulation casting via high valence counterions (DCC–HVCI) using magnesium citrate as a coagulating agent assisted by the hydrolysis of glycerol diacetate. The colloidal behavior of PZT suspensions was evaluated by measuring the zeta potential and the viscosity. The dispersant content and solid loading were optimized to prepare concentrated PZT suspension. The results indicated that PZT suspension with solid loading up to 56vol% can be prepared by the addition of 0.5wt% ammonium polyacrylate at pH=10.6. The critical coagulation concentrations of magnesium and lead in 56vol% PZT suspensions are 15 and 35mM, respectively. The viscosity of 56vol% PZT suspensions with 0.5–1.0wt% magnesium citrate and 2vol% glycerol diacetate is higher than 30Pas at 60°C for 30min which is sufficient to coagulate the suspensions. The coagulating time is 60–90min at 50–70°C. The compressive strength of the coagulated wet samples decreases with the increase of coagulating temperature, but increases with the increase of magnesium citrate content. The strength is in the range 1.5–2.8MPa which is sufficiently high for demolding and handling without deformation. Dense PZT ceramics sintered at 1250–1280°C show homogeneous microstructures with relative densities of 99.2–99.7% and good piezoelectric properties compared with a traditional die pressing method.