Abstract:In preparing stable ceramic suspensions, the interactions of particles and polymer chains should be emphatically considered, which depends on DLVO stabilization theory. However, DLVO stabilization theory are qualitative and lack quantitative methods for judging and predicting stability. The present study introduced a new method for directly judging and predicting suspension stability based on rheological tests and established a correlation between measured data and the state of ceramic suspensions. Among rheological properties, the dominance of the storage modulus G' is more conducive to the realization of steric stabilization, whereas the loss modulus G" exerts a more significant influence in bridging and depletion flocculation states. The stability of suspensions with a given particle size can be judged and predicted by comparing the value of tan δ (the ratio of G" and G') under identical measurement conditions. Lower values of tan δ indicate better stability of the ceramic suspensions. The new method has been verified by experiments of classical alumina suspensions. The results indicate that the alumina suspensions with 14, 17, 20, and 23 vol% of solid particles exhibit optimal stability when combined with PVA concentrations of 3.5, 3.0, 2.5, and 2.0 wt%. Meanwhile, this combination leads to the minimum values of tan δ within the linear viscoelastic region (0.71, 0.45, 0.33, and 0.31, respectively). The universality of the method has been further demonstrated in zirconia suspensions dispersed with Dolapix CE64 dispersant. The application of this method has demonstrated its significance in judging and predicting the stability of ceramic suspensions.

Influence of High Valence Counter-ions on Rheological Properties of Alumina Suspension

Effect of Sequentially Adsorbed Multilayers, Citric Acid(ca)-Pei-ca-pei and PEI-CA-PEI-CA, on the Surface Chemistry and Rheology of Spherical Α-Alumina Suspensions

Direct coagulation casting of alumina suspension by high valence counter ions using Ca (IO 3) 2 as coagulating agent

Influence of bivalent ions on the dispersion and gelation of ceramics suspensions

Direct Coagulation Casting of Alumina Suspension from Calcium Citrate Assisted by Ph Shift

Direct Coagulation Casting of Positively Charged Alumina Suspension by Controlled Release of High Valence Counter Ions from Calcium Phosphate

Reliable High Strength Alumina Fabricated by DCC-HVCI Using Submicron Calcium Citrate Complex

Comparative study on the stabilizing effect of 2-phosphonobutane-1,2,4-tricarboxylic acid and citric acid for alumina suspensions

Direct coagulation casting of alumina using magnesium citrate as coagulating agent with glycerol diacetate as pH regulator

Study On The Rheological Behavior Of Sub-Micron Alumina Aqueous Suspensions

Study on Dispersion Behavior and Its Influence Factors for Alumina Suspension

Direct coagulation casting of alumina suspension via controlled release of high valence counterions from thermo-sensitive liposomes

RHEOLOGICAL BEHAVIOR OF ALUMINA SLURRY

Properties of Alumina Coagulated Bodies Prepared by Direct Coagulation Casting Via High Valence Counter Ions (DCC‐HVCI)

Rheological Characterization of Alumina Ceramic Suspensions in Presence of A Dispersant and A Binder

Rheological Behaviors of Alumina Aqueous Suspensions

Effects of Metal Ions on the Morphology of Calcium Sulfate Hemihydrate Whiskers by Hydrothermal Method

Dispersion and Gelation Properties of Alumina Systems with Isobam Assisted by Dicarboxylic Acids

Hydrophobic coagulation of alumina slurries

A new method for judging and predicting the stability of ceramic suspensions by rheological tests